PA66 GF20 Halogenated FR (A2014D, A2114D) for Engineering Plastics
Nylon 66, filled with 20% of glass fiber and flame resistance halogens, are extruded by Coperion twin-screw extruder is PA66 GF20halogenated FR.
Typical Application of AnmeiPA66 GF20 Halogenated FR (A2014D) (A2015D)
PA66 20% glass fiber and halogenated flame resistance mixed modified grades are very popular to the sectors of highly demanding flame-retardant structural parts, meeting the characteristics of injection molding grade, reinforced grade and flame retardant grade.
The advantage of halogenated FR is low price, good stability, less additive, good compatibility with synthetic resin materials.
Processing Detail of PAGF20Halogenated FR (A2014D)
Other Details of PA66 GF20 Halogenated FR (A2014D)
|
Physical Property |
|
|
Ash |
(20.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1530Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.4-0.6 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.8-1.2% I ISO294-4) |
|
Mechanical Properties |
|
|
Tensile strength (105.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.6% I ISO527) Conditioned |
5mm/ min |
|
Notched Impact Strength (10.0 KJ/m2 I ISO179) Conditioned |
|
|
Flexural Strength (177MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (5050 MPa I ISO178) Conditioned |
2mm/min |
|
Thermal Property |
|
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(245*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
|
|
Injection Molding Conditions |
|
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
280-300°C |
|
Nozzle Temperature |
280-300*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！
Send product request
Other supplier products
 |
PA66 GF20 With High Tensile Strength (A2307D, A2317D) for Engineering Plastics | Elastomer toughened nylon 66 with 20% glass fiber is called PA66 GF20, it shows high oil resistance, high impact resistance, good resistance to low... |
 |
Anmei-Polyamide Nylon 66 (PA66) for Engineering Plastics | Nylon 66 is polyamide 66. The main purpose of Nylon 66 plastic modification is to improve the properties of Nylon 66 material based on the original... |
 |
TPU Slip Masterbatch & Frosted Matte Masterbatch for Engineering Plastics | Anmei company specializes in the production of TPU slip masterbatchingredients and TPU frosted matte masterbatch excellent dispersibility in cast f... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | PA66 GF15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection molding. PA66 GF15 Storage and Handling PRE-PROCESS... |
 |
Anmei-ABS Engineering Plastic | ABSresin is a terpolymer composed of acrylonitrile, butadiene and styrene. ABS has the rigidity, chemical resistance and heat resistance of polyacr... |
Same products
 |
Defoamer Powder | Seller: Shandong Jufu Chemical Technology Co., Ltd. | Antifoaming agent powder primarily serves as an essential component in cement and concrete produc... |
 |
PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | PA66 is nylon 66, namely pa66_gf35is glass fiber. Generally expressed as PA66 GF35, that is, 35% ... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, forinjection moulding. PA66GF3... |
 |
PA66 GF30 Halogen-free FR (A2015F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | Material PA66 GF30FR is a PA66 with 30% glass-fibers and flame retardant free of halogens. This t... |
 |
PA66 GF30 Halogenated FR (A2014F, A2114F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | PA66GF30FR is a Nylon 66 with 30% glass-fibers and flame retardant halogenated. Typical Applic... |