Polyurethane based powder coating MT-PA020G White
Product Description
MT-PA020G is a polyurethane based powder coating, formulated without TGIC and is designed for exterior exposure offering excellent light and weather resistance from a single coat finish.
Powder Properties
| Chemical type | Polyurethane |
| Appearance | Smooth Matt |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.74 ± 0.05 g/cm³ |
| Film Thickness | 75 – 100 microns |
| Coverage | 7.7 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
| Stoving schedule
(object temperature) |
15 – 20 minutes @ 205°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Cold Rolled Steel |
| Pretreatment | B1000 Iron phosphate |
| Film Thickness | 75 – 100 microns |
| Stoving Schedule | 15 minutes at 205°C |
Mechanical Tests
| test | results | |
| Flexibility | ASTM D522 | 12 mm |
| Adhesion | ASTM D3359 | 100% |
| Impact (direct) | ASTM D2794 | 60 kgcm |
| Gloss(@60°） | ISO 2813 | 85 ± 5 |
| Hardness(scratch) | ASTM D3363 | 2H |
| Reflectance Class | DIN EN 16268 | A |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-PA020G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-PA020G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
If you're ready to take the next step, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Send product request
Other supplier products
 |
Valves and pipes powder coating | Introduction The main components are epoxy resin and curing agent. Brief description It is mainly composed of epoxy resin and curing agent. F... |
 |
Silver Gray Color Matte Powder Coating | Powder type Epoxy-Polyester, Polyester Applications Exterior Industrial, Specialized Finish type Smooth Color standard: RAL RAL colors: RAL ... |
 |
Accelerated Dicyandiamide Type Powder CASAMID 783 | Introduction Product: Accelerated Dicyandiamide Type Powder CASAMID 783 Description CASAMID 783 is a powder material of the accelerated dicyandi... |
 |
Flat matte MT-629/62179 | Introduction No. MT-629/62179 Color Brown Surface Flat matte System Super weather-resistant polyester Scope of a... |
 |
Nitrobenzene | Introduction ItemsSpecificationDetection result Appearance Light yellow liquid Light yellow liquid Nitrobenzene content % > ... |
Same products
 |
Sucralose powder Food additive | Seller: Shanghai Yifu Food Ingredients Co., Ltd | Sucralose, as a new generation of high-sweetness sweetener, has demonstrated comprehensive and ou... |
 |
Sucralose Purchase price | Seller: Shanghai Yifu Food Ingredients Co., Ltd | Sucralose, as a high-sweetness, calorie-free, and highly stable artificial sweetener, enjoys wide... |
 |
Sucralose Partners, long-termCooperation | Seller: Shanghai Yifu Food Ingredients Co., Ltd | Sucralose is currently a widely used high-potency sweetener globally. Its safety has been verifie... |
 |
Sucralose Marke quotation | Seller: Shanghai Yifu Food Ingredients Co., Ltd | Sucralose is a high-sweetness agent obtained by replacing the hydroxyl groups at positions 4, 1',... |
 |
Sucralose Supply price | Seller: Shanghai Yifu Food Ingredients Co., Ltd | Sucralose is a trichloro derivative of sucrose (4,1',6'-trichloro-4,1',6'-dideoxy-galactosucrose)... |