Polyurethane based powder coating MT-PA020G White
Product Description
MT-PA020G is a polyurethane based powder coating, formulated without TGIC and is designed for exterior exposure offering excellent light and weather resistance from a single coat finish.
Powder Properties
| Chemical type | Polyurethane |
| Appearance | Smooth Matt |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.74 ± 0.05 g/cm³ |
| Film Thickness | 75 – 100 microns |
| Coverage | 7.7 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
| Stoving schedule
(object temperature) |
15 – 20 minutes @ 205°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Cold Rolled Steel |
| Pretreatment | B1000 Iron phosphate |
| Film Thickness | 75 – 100 microns |
| Stoving Schedule | 15 minutes at 205°C |
Mechanical Tests
| test | results | |
| Flexibility | ASTM D522 | 12 mm |
| Adhesion | ASTM D3359 | 100% |
| Impact (direct) | ASTM D2794 | 60 kgcm |
| Gloss(@60°） | ISO 2813 | 85 ± 5 |
| Hardness(scratch) | ASTM D3363 | 2H |
| Reflectance Class | DIN EN 16268 | A |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-PA020G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-PA020G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
If you're ready to take the next step, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
在线联系供应商
Other supplier products
 |
Instrument powder Coating | Introduction It is made of polyester resin and epoxy resin as the main base materials, and has the excellent decorative, mechanical properties and... |
 |
Powder coating for construction machinery | Introduction Engineering machinery is an important part of the equipment industry. Engineering machinery can be seen in major areas related to nat... |
 |
High durability powder coatings MT-810 AM | Product Description MT-810 AM is a series of high durability powder coatings, formulated without TGIC, designed for exterior exposure. Tested agai... |
 |
Polyurethane powder coating series | Made of hydroxy polyester resin and isocyanate curing agent as the main raw materials. Features: –Good adhesion, good mechanical properties... |
 |
Aluminium Powder Coating | Aluminium Powder Coating Powder coating is a system of protection of the aluminum that consists in the application of a coating, either liquid or ... |
Same products
 |
5.4,4'-Oxydiphenol CAS 1965-09-9 | 卖方: Yufeng International Group Co., Ltd | Product Name: 4,4'-Oxydiphenol Synonyms: 4,4'-Dihydroxydiphenyl ether 4,4'-Oxydiphenol Bis(4-... |
 |
1,1,2,2-Tetrachloroethane CAS 79-34-5 | 卖方: Yufeng International Group Co., Ltd | Product Name: 1, 1, 2, 2-Tetrachloroethane Synonyms: 79-34-5 s-Tetrachloroethane Acetylene te... |
 |
3.Chlorotrifluoroethylene (CTFE) CAS 79-38-9 | 卖方: Yufeng International Group Co., Ltd | Synonyms: CHLOROTRIFLUOROETHYLENE 79-38-9 CTFE Chlorotrifluoroethene 1-Chloro-1,2,... |
 |
2.1,1,2-Trichloroethane CAS 79-00-5 | 卖方: Yufeng International Group Co., Ltd | Product Name: 1, 1，2-Trichloroethane CAS: 79-00-5 Synonyms:79-00-5, Vinyltrichloride, beta-... |
 |
1.1,1,2,2-Tetrachloroethane CAS 79-34-5 | 卖方: Yufeng International Group Co., Ltd | Product Description Product Name: 1, 1, 2, 2-Tetrachloroethane Synonyms: 79-34-5 s-Te... |