Basecoat powder coating
Powder Properties
| Chemical Type | Polyester |
| Area of usage | Automotive trim parts,roof rail systems |
| Particle Size Distributon | Custom manufactured |
| Appearance | Smooth, satin |
| Colour | Silver metallic |
| Density (g/cm3) | 1.17 ± 0.05 |
| Stoving schedule | 10 minutes at 200°C (time at object temperature) |
| Application | Electrostatic |
| Storage Stability | under dry, cool (<25°C) conditions, at least 24 months from production date |
Test Conditions
The results are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Steel panels, Aluminium |
| Pretreatment | Bonder (WH/60/OC) iron phosphate, Bonder (722/W/OF) |
| Film thickness | 70 µm |
| Cure schedule | 10 minutes 200°C |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease. For maximum protection it is essential to pre-treat components prior to the application of MT-A2204 basecoat. Iron Phosphate and Zinc Phosphate of ferrous metals improve corrosion resistance. Aluminium parts require a chromate conversion pre-treatment.
Application
MT-A2204 basecoat powders can be applied by manual or automatic electrostatic spray equipment. Tribo application is not recommended. It is recommended that for consistent application and appearance product be fluidized during application. MT-MW188I must be fully cured otherwise there may be a loss of metallic effect or discoloration of the clear topcoat. MT-MW188I is not stabilized for direct gas fired ovens.
• All coated pieces should be handled with clean lint free gloves.
• Parts should not be stored in an environment with high humidity.
• Clear coat should be applied as soon as possible after metallic application (maximum time between coats is 8 hours)
• Parts should not be passed through a pre-treatment process prior to application of the clear coat Despite the fact that MT-MW188I is a bonded metallic it is not recommended to recycle the powder.
在线联系供应商
Other supplier products
 |
Iron Oxide Pigment MT-645T | Description TypeBrown pigment – High Performance, special with high thermal stability Delivery form Powder Chemical class ... |
 |
High Insulation Epoxy Powder Coating | Product Overview High Insulation Epoxy Powder Coating is a thermoset epoxy-based coating system developed to provide you with strong dielectric pe... |
 |
Metallic flat matte MT-039/98992 | Introduction No. MT-039/98992 Color Metallic silver Surface Metallic flat matte System Weather-resistant polyester ... |
 |
Polyester Powder Coatings – Full Product Range | Product Categories CategoryExamples / SystemsTypical Application By Resin Type Unsaturated Polyester Powder Coating Decorative and fu... |
 |
Navy Blue Sand Texture Powder Coating | Introduction Key attributesDetails Brand STD Place of Origin China Main Raw Material EPOXY Usage Furniture Paint, Ca... |
Same products
 |
High Concentration Plastic Color Masterbatch Factory Direct Supply | 卖方: 861445 | We are a professional color masterbatch manufacturer with years of R&D experience in plastic ... |
 |
Acid Ink Blue G Factory | 卖方: TIANJIN LEADING IMPORT & EXPORT CO., LTD | Acid Ink Blue G Factory 【Application of Acid Ink Blue G 】 mainly used for making blue or ... |
 |
Acid Black ATT Factory | 卖方: TIANJIN LEADING IMPORT & EXPORT CO., LTD | Acid Black ATT Factory 【What’s Acid Black ATT】 is made of acid black 10B and acid o... |
 |
Acid Black 10B Factory | 卖方: TIANJIN LEADING IMPORT & EXPORT CO., LTD | Acid Black 10B Factory is mainly suitable for dyeing and printing wool ,silk and nylon fabri... |
 |
Sulphur Dyes | 卖方: TIANJIN LEADING IMPORT & EXPORT CO., LTD | Sulphur Dyes BuyDye supplies a range of sulphur dyes for cotton-based textile dyeing, includ... |