Tempered glass Toughened glass Safety glass processed glass Polished
PRODUCTION PROCESS:
In the production of flat glass, the molten silica-based mix is cooled slowly under carefully controlled conditions. This annealing procedure removes undesirable stresses from the glass. Cooling occurs in an annealing "lehr"; and then annealed glass is heated to a temperature near its softening point and forced to cool rapidly under carefully controlled conditions. The heat treating process produces highly desirable conditions of induced stress, which result in additional strength, resistance to thermal stress, and impact resistance.
FEATURE:
1. Safety, once broken, it splits into tiny harmless pieces.
2. Hardness, 4 times harder than ordinary float glass.
3. Special logo and pattern can be printed on tempered glass.
4. Outstanding performance in resisting thermal stress and wind-load.
5. Bear sudden temperature change of 220 centigrade degree.
SPECIFICATIONS:
Thickness: 3——19mm
Sizes: Max. size: 2440x5000mm
APPLICATION:
1. Traffic vehicles, such as the windows of train, bus, car etc
2. Architecture, such as windows or other areas in a building
3. Household appliances and furniture, such as glass table top and show shelves.
NOTICE:
1. Tempered glass can not be cut, drilled or other further process.PRODUCTION PROCESS:
In the production of flat glass, the molten silica-based mix is cooled slowly under carefully controlled conditions. This annealing procedure removes undesirable stresses from the glass. Cooling occurs in an annealing "lehr"; and then annealed glass is heated to a temperature near its softening point and forced to cool rapidly under carefully controlled conditions. The heat treating process produces highly desirable conditions of induced stress, which result in additional strength, resistance to thermal stress, and impact resistance.
FEATURE:
1. Safety, once broken, it splits into tiny harmless pieces.
2. Hardness, 4 times harder than ordinary float glass.
3. Special logo and pattern can be printed on tempered glass.
4. Outstanding performance in resisting thermal stress and wind-load.
5. Bear sudden temperature change of 220 centigrade degree.
SPECIFICATIONS:
Thickness: 3—19mm
Sizes: Max. size: 2440x5000mm
APPLICATION:
1. Traffic vehicles, such as the windows of train, bus, car etc
2. Architecture, such as windows or other areas in a building
3. Household appliances and furniture, such as glass table top and show shelves.
NOTICE:
1. Tempered glass can not be cut, drilled or other further process.
Other supplier products
|
|
3mm 4mm 8mm Patterned glass for door window Furniture |
PRODUCTION PROCESS: Using the high quality raw materials from both domestic and abroad, such as the silica sand, soda ash, salt cake, dolomite, e... |
|
|
Low-E glass Low emissivity glass Coated glass Reflective glass Radiation protection |
PRODUCTION PROCESS: What's Low-E Glass? Low emissivity coated glass is also called Low-E glass.There are two types of Low-E glass: hard coat and so... |
|
|
3 4 5 6 8mm Clear Diamond Patterned Glass for window furniture door |
PRODUCTION PROCESS: Using the high quality raw materials from both domestic and abroad, such as the silica sand, soda ash, salt cake, dolomite, e... |
|
|
4mm 5mm Dark blue Reflective float glass Coated glass Building glass |
PRODUCTION PROCESS: It is produced by using CVD technology (chemical vapor deposition) that creates a perfectly uniform layer of metal oxide chem... |
|
|
PVB 0.38mm,0.76mm,1.14mm Laminated Explosion-proof anti-theft anti-ultraviolet used for safety glass |
PRODUCTION PROCESS: It is manufactured by permanently bonding two or more lites of glass with layers of polyvinyl butyral (PVB) interlayer, under... |