Bimetallic Wear Plates
Bimetallic wear plateare unique wear resistant materials in that they combine very high wear resistant qualities of a white iron (ASTM A532 15%CrMo, 700BHN – 63HRc) with a weldable &high impact toughness mild steel through a metallurgical bond to create a product that is exceptionally resistant to impact and abrasion while retaining. The typical property is as below:
Tensile Strength 630Mpa Min.
Shearing Strength 250Mpa Min.
Hardness 63 HRC/700BHN
The micro-structure is Carbide + Martensite + Retained Austenite, the carbide’s content is about 41.5%. The bimetallic wear plate, a component made by forging, is widely used in feeder chute and hopper wear protection situations.
Why Choose WALKSON Bimetallic Wear Plates
Super high level wear-resistant ability
Custom made size to suit your need
Very stable brazing welding quality
As one of the mostprofessional manufacturing as a service companies,we provide manufacturing services china, undercarriage parts, steel foundry chinaetc.want to know more about manufacturing services in china, please contact us.
在线联系供应商
Other supplier products
 |
Sprocket/ Tumbler | The sprocketis made from low alloy high strength steel, combined with quenched and tempered heat treatment plus induction hardened to get the requi... |
 |
White Iron Liners | We can provide a wide range of wear resistant products for mineral processing industry. The role of a white iron mill lineris to give the mill head... |
 |
Hot Forging | Hot forging is also called hot die forgingby hot forging manufacturers. During the hot die forging process, the deformed metal flows violently and ... |
 |
Ni-hard Wear Liners/ Billets | Ni Hard Liners/ Billets NiHard is a well-established white iron product alloyed with nickel and chromium to give significant abrasion and impact r... |
 |
Rigging Components | WALKSON manufacture most parts of the dragline rigging componentsand structural component for buckets used in the surface mining industry. Whether ... |