Degassing Flux
Degassing Flux(SATA-PF-350)
General Description of Degassing Flux (SATA-PF-350)
Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process.
SATA-degassing flux is a kind of traditional high efficiency aluminum degassing fluxand its alloys, it used for removing hydrogen and oxides from the aluminium melting.
Application of Degassing Flux (SATA-PF-350)
Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten.
Advantage of Degassing Flux (SATA-PF-350)
Easy operation, There are two options. One is with hexachloroethane in tablet form.and another is in powder form without hexachloroethane
It has excellent performance in refining, degassing and drossing
It can enhance the quality of casting, hydrogen content of aluminium molten can reduce to ≤0.1ml/100gAl, the oxide inclusion(Al2O3) can reduce 20% min, the casting inclusion defect reduce 50%min
Specification of Degassing Flux (SATA-PF-350)
White mixed powder
It is suit for all series alloy except high magnesium alloy,
Dosage: recommended dosage: 3%-5% large melting furnace, 4%-6% for crucible furnace
Working Temperature: 710℃-780℃
Package of Degassing Flux (SATA-PF-350)
Packed in 5kg (PE), 25kg (PP), 1000kg bags or customized.
Stored in dry, well-ventilated place, and avoid direct sunlight, keep sealed before using.
NOTE: This flux has serious hygroscopicity, please use immediately after opening.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Fluxes for Magnesium Alloy | Magnesium alloy has a low melting point and small heat capacity. When heated in the air, it gets oxidized fast, and it is easy to burn when overhea... |
 |
Aluminium Titanium Boron-Al-Ti-B Grain Refiner | General description of Aluminium Titanium Boron-Al-Ti-B Grain Refiner In casting applications, the control of grain size is very critical in mai... |
 |
Covering Flux- C11 | The function of Covering Flux- C11 C11 is fused flux, suitable for all kinds of aluminum and aluminum alloy except those containing high-magnesium... |
 |
Anhydrous Magnesium Chloride | Magnesium Chloride Anhydrous (AMC) General Description of Magnesium Chloride Anhydrous (AMC) Name: Magnesium Chloride Anhydrous (AMC) By-product of... |
 |
granulated-fused-refining-fluxes | General Introduction: SATA granulated fused refining flux is a eutectic salt composed of mgcl2 anhydrous and potassium or sodium chloride. Which ... |