CA Series-330CA30 PEEK Carbon Fiber Reinforcement
CA Series-330CA30 PEEKFC, CFPEEKcarbon fiber reinforcement is suitable for the production of bushing seals and other products, can be faster from the bearing surface heat dissipation, at the same time has a high thermal deformation temperature (336 ° C) , also can maintain strength at high temperature, to a certain extent, can replace metal materials.
Specification of CA Series-330CA30 PolyetheretherketoneCarbon Fiber Reinforcement
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
|||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
℃ |
343 |
|
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
|
Amorphous |
gcm-3 |
|||
|
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
|
by immersion |
Equilib riu m,23℃ |
% |
||
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
|
23℃,50kHz |
3 |
|||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
Ω cm |
10 9 |
||
As one of peek suppliers, we will do our best to meet all the needs of customers.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
CA Series-550CA30 PEEK Carbon Fiber Reinforcement | CA Series-550CA30 carbon peekreinforcement is a 30% carbon fiber reinforced naturalPEEK material, the addition of carbon fiber significantly increa... |
 |
Grade CA Carbon Fiber Reinforcement PEEK | PEEK-CA series reinforced plastics filled with carbon fiber, high elastic modulus, mechanical strength, creep resistance, wear resistance and dynam... |
 |
Grade G PEEK Pure Resin Pellets | With good toughness and impact resistance, Grade G peek pelletscan be disinfected using steam, ethvi alcohol and rays, etc. You can see the wide us... |
 |
Dental Tooth Materials PEEK R&D Series | Dental PEEKMaterialR&D Series has good wear resistance and high mechanical strength. It is mainly used in dentistry in medical field. Specif... |
 |
Peek in Bearing Material | Peek Bearing Material Due to its excellent mechanical strength, dynamic fatigue resistance, high-temperature resistance, creep resistance, self-... |