Polyester based powder coating MT-OA110G
Product Description
MT-OA110G is a polyester based powder coating, formulated without TGIC.
Powder Properties
| Chemical type | Polyester TGIC-free |
| Appearance | Smooth Matt |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.53-1.63 g/cm³ |
| Film Thickness | 75 – 100 microns |
| Coverage | 7.8 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
| Stoving schedule
(object temperature) |
10 minutes @ 200°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Gold Seal polished steel |
| Pretreatment | Lightweight Zinc phosphate |
| Film Thickness | 70 – 80 microns |
| Stoving Schedule | 10 minutes at 200°C |
Mechanical Tests
| test | results | |
| Flexibility | ISO6860 | 5mm |
| Erichsen cupping | ISO1520 | 6mm |
| Adhesion | ISO2409 | 100% |
| Impact (dir/rev) | ISO 6272 | 30/30 kgcm |
| Gloss(@60°） | ISO 2813 | 30±5% |
| Hardness(Buchholz) | ISO2815 | 8-125 |
| Reflectance Class | DIN EN 16268 | A |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-OA110G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-OA110G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
If you're ready to take the next step or Request Free Samples, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Sand grain matte MT-039/67495 | Getaquote whats/app：+86 132 6275 2056 WEB: std-coatings.com No. MT-039/67495 Color Brown Surface Sand grain matte Syst... |
 |
Solvent Type Epoxy Resin STD-BE236X80 | Introduction： STD-BE236X80 is a bisphenol A solvent based epoxy resin,used with polyamide curing agent to produce high-quality anti-corrosion pain... |
 |
filter element powder Coating | Getaquote whats/app：+86 132 6275 2056 WEB: std-coatings.com Accurate selection of powder has always been a problem for the powder industry. To solv... |
 |
Wood grain transfer powder coating | Product introduction: Transfer powder coating can form various patterns or patterns on the coating on the substrate through transfer technology. T... |
 |
Bonded Metal Powder Coatings | Introduction Bonded metal powder coatings integrate metal pigments with resin and additives via thermal bonding, offering metallic finishes that b... |
Похожие товары
 |
Hot Melt Adhesive for Vacuum Insulation Panels | Продавец: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Vacuum Insulation Panels Supply & Technical Support Capabilities ... |
 |
Hot Melt Adhesive for Packaging | Продавец: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Packaging Bond Strength & Durability: Hot melt adhesives provide i... |
 |
Hot Melt Adhesive for Hygiene Products | Продавец: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Hygiene Products refers to thermoplastic pressure‑sensitive adhesives ... |
 |
LSAW Steel Pipe & Tube | Продавец: HEBEI TIRICO PIPELINE CO.,LTD | LSAW Steel Pipe & Tube , or Longitudinal Submerged Arc-Welding Pipe (also known as SAWL ... |
 |
Anti-Corrosion Steel Pipe & Tube | Продавец: HEBEI TIRICO PIPELINE CO.,LTD | Anti-Corrosion Steel Pipe & Tube Anti-Corrosion Steel Pipe & Tube What Is an Anti... |