Glass-To-Metal Sealed Alloy
Precision Alloy 4J42/4J48/4J52The application of Precision Alloy 4J42/4J48/4J52 : It is applied to soft glass-to-metal and ceramic-to-metal seals in electronic component.*Alloy 42,Website: F30,UNS k94100,(Fe-42Ni),Chinese 4J42*Alloy 52,ASTM F30,UNS K95050, (Fe-50Ni),Chinese 4J50*sealmet HC-4,,alloy426, ASTM F31,UNS k94760, (Fe-42Ni-6Cr),Chinese 4J6Usage: It is applied to soft glass-to-metal and ceramic-to-metal seals in electronic component.Table 1 Grade & Chemical CompositionGradeGrade & Chemical Composition(%)CPSMnSiBAlCoNiCrFe4J60.050.0200.0200.250.300.2041.5~42.55.50~6.30Balance4J470.050.0200.0200.400.3046.8~47.80.80~1.40Balance4J490.050.0200.0200.400.300.0246.0~48.05.00~6.00Balance4J420.050.0200.0200.800.300.101.041.5~42.5Balance4J450.050.0200.0200.800.300.1044.5~45.5Balance4J500.050.0200.0200.800.300.1049.0~50.5Balance4J520.050.0200.0200.600.30-51.5~52.5Balance4J540.050.0200.0200.600.30--53.5~54.5BalanceNotes: 1,Under condition that the average coefficient of the linear expansion meets the requirements of the standard, the content of nickel and cobalt are allowed to deviate from the stated range. 2,The shape and dimensions of the alloys are in compliance with YB/T5235.Table 2 Heat Treatment & Coefficient of Linear ExpansionGradeHeat Treatment System of the SamplesAverage Coefficient of Linear Expansion20-300 C20~400 C20-450 C4J6To be heat treated at a temperature of 1130 20 C in the hydrogen, hold for 15 min., cool to 200 C at a rate less than 5 C/min7.6~8.39.5~10.24J478.1~8.74J498.6~9.39.4~l0.14J42To be heat treated at a temperature of 900 20 C in the hydrogen, hold for 1h, cool at a rate less than 5 C/min to 200 C4.0~5.06.5~7.54J456.5~7.26.5~7.24J509.2~10.09.2~9.94J52To be heat treated at a temperature of 850 20 C in the hydrogen, hold for 1h, cool at a rate less than 300 C/H to 400 C9.8~11.09.8~11.04J5410.2~11.410.2~11.4Table 3 Typical Expansion CoefficientGradeAverage Coefficient of Linear Expansion /(10-6/K)20~100 C20~200 C20~300 C20~400 C20~450 C20~500 C20~600 C4J66.87.07.79.711.112.24J478.18.68.38.39.110.04J499.09.08.99.610.911.84J425.64.94.85.96.97.89.24J457.57.57.17.27.18.39.54J509.89.89.59.49.710.64J5210.310.410.210.310.310.310.84J5410.712.710.710.810.310.811.2Size Range:1.Sheet---Thickness 0.1mm~3.5mm, width: 300mm,Condition: cold rolled, bright, bright annealed2.Plate---Thickness 3.5mm~40.0mm,width: 300mm,Condition: cold rolled, hot rolled, annealed3.Round Wire---Dia 0.1mm~Dia 5.0mm,Condition: cold drawn, bright, bright annealed4.Flat Wire---Dia 0.5mm~Dia 5.0mm,length: 1000mm,Condition:flat rolled, bright annealed5.Bar---Dia 5.0mm~Dia 8.0mm,length: 2000mm,Condition:cold drawn,bright, bright annealed---Dia 8.0mm~Dia 32.0mm,length: 2500mm,Condition:hot rolled,bright, bright annealed---Dia 32.0mm~Dia 180.0mm,length: 1300mm,Condition:hot forging,peeled, turned, hot treated6.Capillary---OD 8.0mm~1.0mm,ID 0.1mm~8.0mm,length: 2500mm,Condition: cold drawn, bright, bright annealed7.Pipe---OD 120mm~8.0mm,ID 8.0mm~129mm,length: 4000mm,Condition: cold drawn, bright, bright annealed
Другие товары поставщика
|
|
|
High Temperature Nickel AlloyNickel-Chromiun High temperature alloys*Alloy A286,Website: S66286,SAE AMS 5726,Chinese GH2132*Inconel 600,ASTM B564,U... |
|
|
|
Magnetic BarMagnetic bar is used to separate very fine ferrous particles,Website:, ferrous chips and other ferrous material from solid, powder or l... |
|
|
|
Bonded Ferrite MagnetBonded Ferrite magnet is made by mixing the ferrite powder with polymer plastic (such as PA,Website:, PPS, etc.,), then throug... |
|
|
|
Hysteresis alloys (Iron-Cobalt- Vanadium)Representive Grades: 2J4,Website:, 2J7, 2J10, 2J11, 2J51, 2J52, 2J53Note: A ductile, semi-hard magnetic al... |
|
|
|
AlNiCo magnet are a type of metal alloy,Website:, which is derived from Aluminum, Nickel, Cobalt, Iron and a few other elements, such as: Copper, T... |
Все товары поставщика
Похожие товары