GRC/GFRC/GRG/FRP Molding Silicone Rubber Compounds with Low Shrinkage and High Tear Strength
GRC/GFRC/GRG/FRP Molding Silicone Rubber Compounds with Low Shrinkage and High Tear Strength
1. Introduction for GRC/GFRC/GRG/FRP Molding Silicone Rubber Compounds with Low Shrinkage and High Tear Strength
We Hong Ye Silicone Rubber Company deal with selling silicone compounds all over the world and we provide our buyers with:
1). the best prices for products being supplied
2). the best terms of delivery
3). customer support 2. Services for GRC/GFRC/GRG/FRP Molding Silicone Rubber Compounds with Low Shrinkage and High Tear Strength
Besides, We Hong Ye Silicone Rubber Company are ready to teach your specialists how to make up silicone molds themselves. And it does not matter whether you are our constant customer or it is the first time you contact us, whether you are going to buy one kilo of products or a big lot thereof - you can be absolutely sure that you will find right what you need with us. Our Silicone rubber materialsare widely used for sculptures, training models, park and garden sculptures etc.
3. Application for GRC/GFRC/GRG/FRP Molding Silicone Rubber Compounds with Low Shrinkage and High Tear Strength
1). Our Hong Ye Silicone Rubber are used for
as silicones used to produce flexible molds
as filling compounds
as dressing compounds to produce molds in manufacture of foot wear.
4. Features for GRC/GFRC/GRG/FRP Molding Silicone Rubber Compounds with Low Shrinkage and High Tear Strength
Main benefits of silicones used to produce flexible molds:
1). wide range of operating temperatures: from -60C to +250C
2). tolerance to environmental exposure
3). high tear resistance
4). do not cause corrosion of metals and alloys, including copper
5). compatibility with most filling materials
6). precise reproduction of surface details
7). stability
5. Brief specifications for GRC/GFRC/GRG/FRP Molding Silicone Rubber Compounds with Low Shrinkage and High Tear Strength
We have very soft and very liquid silicone compound;
We have silicone compound with average viscosity and average hardness;
We have soft and liquid silicone compound, with very high elongation at break;
We have silicones used for vertical surfaces;
We have silicones molds making for further casting not only of gypsum, soap, paraffine, polymer clay, acryl and polyester resins but also cement and epoxy resin etc.
HY-6 series:Model: HY- 620
Appearance: white
Mixing proportion of curing agent (%): 5%
Operating time (mins 25 0C ): 30-50
Curing time(hours 25 0C): 3-5
Hardness (A°) : 20±2
Viscosity (Mpas -25 0C): 12000~14000
Tensile-strength(Mpa): >2.8
Tear-strength (KN/m): >32
Elongation-break(%): >420
Linear Shrinkage (%): <0.3Model: HY- 625
Appearance: white
Mixing proportion of curing agent (%): 5%
Operating time (mins 25 0C ): 40-70
Curing time(hours 25 0C): 4-7
Hardness (A°) : 25±2
Viscosity (Mpas -25 0C): 17000~19000
Tensile-strength(Mpa): >3.2
Tear-strength (KN/m): >27
Elongation-break(%): >440
Linear Shrinkage (%): <0.3Model: HY-630
Appearance: white
Mixing proportion of curing agent (%): 5%
Operating time (mins 25 0C ): 60-90
Curing time(hours 25 0C): 5-7
Hardness (A°) : 30±2
Viscosity (Mpas -25 0C): 27000~32000
Tensile-strength(Mpa): >4.2
Tear-strength (KN/m): >30
Elongation-break(%): > 440
Linear Shrinkage (%): <0.3Model: HY- 640
Appearance: white
Mixing proportion of curing agent (%): 3%-5%
Operating time (mins 25 0C ): 40-70
Curing time(hours 25 0C): 4-7
Hardness (A°) : 40±2
Viscosity (Mpas -25 0C): 30000~38000
Tensile-strength(Mpa): >4.50
Tear-strength (KN/m): >30
Elongation-break(%): > 420
Linear Shrinkage (%): <0.3
E-6 series
Model: E-620
Appearance: Translucent
Hardness(shore A): 20±2
Mix ratio(A:B): 1:1/10:1
Viscocity Part A(mPa.s): 23000±2000
Viscocity Part B(mPa.s): 3500±500
Tensile strength (kgf/cm2): 45±5
Tear-strength (kN/m): 20±2
Elongation(%): 500±50
Pot life/working time (mins): 30-40
Curing time/setting time (hrs): 3-4hrs(25°C)
110-20mins(60°C)
Shrinkage rate (%): 0.1Model: E-625
Appearance: Translucent
Hardness(shore A): 25±2
Mix ratio(A:B): 1:1/10:1
Viscocity Part A(mPa.s): 27000±2000
Viscocity Part B(mPa.s): 3500±500
Tensile strength (kgf/cm2): 48±5
Tear-strength (kN/m): 22±2
Elongation(%): 500±50
Pot life/working time (mins): 30-40
Curing time/setting time (hrs): 3-4hrs(25°C)
110-20mins(60°C)
Shrinkage rate (%): 0.1Model: E-630
Appearance: Translucent
Hardness(shore A): 30±2
Mix ratio(A:B): 1:1/10:1
Viscocity Part A(mPa.s): 25000±2000
Viscocity Part B(mPa.s): 2400±500
Tensile strength (kgf/cm2): 50±5
Tear-strength (kN/m): 18±2
Elongation(%): 450±50
Pot life/working time (mins): 30-40
Curing time/setting time (hrs): 3-4hrs(25°C)
110-20mins(60°C)
Shrinkage rate (%): 0.1Model: E-640
Appearance: Translucent
Hardness(shore A): 40±2
Mix ratio(A:B): 1:1/10:1
Viscocity Part A(mPa.s): 30000±2000
Viscocity Part B(mPa.s): 6000±500
Tensile strength (kgf/cm2): 65±5
Tear-strength (kN/m): 16±2
Elongation(%): 450±50
Pot life/working time (mins): 30-40
Curing time/setting time (hrs): 3-4hrs(25°C)
1 110-20mins(60°C)
Shrinkage rate (%): 0.1
If you want additional information, vast number of informative articles about silicones and their application, If you would like to know more about silicones and make a proper choice, contact Kaka below:Email:hysa(at)szrl.net
Mob: