Rail Transit Interior powder coating MT-A700 series
Product overview
A series of products designed for rail transit internal and external parts. Application: Suitable for spraying of multi-structure interior and exterior parts of rail transit
Coating characteristics:
Excellent leveling
Excellent UV and salt spray resistance
Good easy-to-clean function
Application parameters:
Atomization air pressure: ~0.7bar
Primary air pressure: ~0.7bar
Recommended voltage: 40-90KV
Secondary rework:
Surface treatment: grinding + air cleaning
Recoating mode: Reduce spraying voltage
| Chemical type | External part: polyester type
Internal part: polyester epoxy mixed type |
| Appearance | External part: color depends on customer requirements
Internal part: mainly metallic silver and wood grain powder and white plane |
| Particle size | Depends on product type and color |
| Gloss | Depends on product |
| Specific gravity | 1.2-1.8g/CM’ (related to color) |
| Storage conditions | v30P sealed in a dry and cool place |
| Validity period | 12 months (v30°C) |
| Curing conditions (workpiece temperature) | 180*15 minutes, 200*10 minutes |
| Item | Instrument | Judgment standard | Test standard |
| Adhesion | Single-edged knife, tape | 0 crack | GB/T 9286
ISO 2409 |
| Impact resistance | Impact tester | 50 kg.cm (0 8mm )
2.5Nm (016mm) |
GB/T 1732
ASTM D 2794 ISO 6272 |
| Coating hardness | Hardness tester | *1H | GBZT6739 ASTM 03363 |
| Alkali resistance | 0.1N NaOH. Beaker | M48H, coating has no blistering, shedding, rust, or spots | GB/T9274 |
| Acid resistance | 0.1N acid, beaker | M24H, coating does not become mushy | GB/T9274 |
| Salt spray resistance | NSS fog box | *500H, rust and blister < 2mm | GB/T 1771 ASTMB-117 ISO 7253 |
| Humidity and heat resistance | Constant temperature and humidity box | a 500H, slight discoloration is allowed, no blistering, rust, or shedding | GB/T 1740 ISO 6270 |
| Weather resistance | Artificial accelerated aging box | OUV-B313500H M 3 level | GB” 1865 ISO 11341 |
| Water resistance | Steaming water | 20 cycles allow coarsening, but no blistering | GB/T1733 ASTM D 2247 |
| Flame retardancy | Third-party test | ISW35 | ASTM E162 |
| Third-party test | DS(1.5)W1OO DS(4.0)W165 | ASTME662 | |
| Third-party test | V0 grade | UL-94 |
• The above tests all use 0.8mm degreased and derusted cold-rolled steel plates, with a coating thickness of 60~80um. The performance indicators of the coating will vary slightly with different gloss.
Environmental requirements:This product does not contain heavy metals such as tin, selenium, lead, hexavalent tantalum, mercury, zinc, cadmium, etc., and fully complies with RoHS 2.0 environmental protection requirements.
Note:We will provide complete powder coating consultation and customized application solutions according to the actual needs of each customer. The test indicators mentioned in this report are the data obtained by laboratory testing and are for reference only, not as performance commitments for product applications. The results will vary with environmental factors and electrical stacking.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Blue Sand Texture Powder Coating | What is Powder Coating? Powdercoating is a new type of 100% solid powder coating which does not contain solvents. With no solvent, no pollution, e... |
|
|
Pure polyester/Primid type powder coating series | Introduction: Introduction: Made of polyester resin and Primid curing agent as the main raw materials. Features: –Good adhesion and excell... |
 |
Comprehensive water treatment agent STD-10 | The comprehensive water treatment agent STD-10 is a multifunctional additive with the following characteristics: synergistic effect, which can cont... |
 |
High-Purity Hydrogen (H₂) | Introduction High-purity hydrogen (H₂), typically defined as hydrogen with a purity level of 99.999% or higher, is a critical resource in various ... |
 |
Charm Deep Love Green powder coating | Product Features With a special skin feel formula, the surface of the coating after powder solidification has a touch similar to that of the skin,... |