Powder coating primer containing zinc MT-PZ ALZ44TH
Product Description
MT-PZ is a powder coating primer containing zinc which is designed to give enhanced corrosion protection of mild steel. This duplex system combines cathodic protection and barrier effect. Dedicated to steel protection with a surface pre-treatment obtained by grit/shot. MT-PZ is based on a specific epoxy zinc rich formulation that brings conductivity to enable the cathodic protection. MT-PZ includes a specific anticorrosive function which improves the protection in case of scratch.
Powder Properties
| Chemical type | Thermosetting epoxy |
| Appearance | Smooth |
| Color | Grey |
| Recommended Film Thickness (µm) | 70 – 120 µm |
| Density (g/cm3) | 2.9 ± 0.03 g/cm³ |
| Application | Electrostatic |
| Storage | Under dry, cool (≤ 30°C) conditions |
| Shelf life | At least 12 months from production date |
Pretreatment
Surface preparation depends upon the metal, the type of surface, its conditions and the required performance. See our recommendation for pretreatment to be used with MT- PZ.
| Substrate | Mechanical pretreatment | Chemical pretreatment |
| Mild steel | Grit Blasting Sa 2.5 in accordance with ISO NF EN 8501-1. Roughness: Rz 35 60 µm / Ra 6-12 µm | Banned |
| Cast steel | ||
| Electro Zinc steel | Banned | |
| Hot dip galvanized steel | ||
| Zinc sprayed (gas flame/electrical deposition) |
Application
MT-PZ is suitable for corona electrostatic spraying. Tribo application is not recommended.
| Application settings | Fluidizing air pressure: 1.5kg/cm2 initially then 1kg/cm2 Transport air pressure: 0.5 to 0.8 kg/cm Recommended voltage: 65 to 70kV |
| Curing limits | Primer should be cured, or at least gelled, using the recommended curing schedules, before application of the topcoat. The object temperature must not be below 110°C or above 180°C. The primer should be cured in a convection oven, optionally with infra-red heaters, with air temperature not exceeding 180°C. |
| Recommended film thickness | 70-120 µm A good protection is linked with the recommended film thickness. |
| Recycling | Trials, with suitable recycling equipment, must be carried out before commencing production. Attention should be paid to the ratio of new powder, a minimum of 70% must be used. Gun nozzles must be cleaned every 30 minutes. |
If you're ready to take the next step or Request Free Samples, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
|
|
Functional anti-corrosion powder coating | Brief description: Made of epoxy resin and curing agent as the main base materials Features: Highly active, fast curing, excellent anti-corrosio... |
|
|
Metallic plane MT-629/93601 | Introduction No. MT-629/93601 Color Gray Surface Metallic plane System Resin imported from Austria Packing Speci... |
 |
Indoor powder coatings | Introduction Indoor powder coatings are environmentally friendly and highly efficient finishing solutions. They are applied as a dry powder and th... |
 |
High-Performance Metal Bonding Powder Coating | Introduction A specialized upgrade of metallic powder coatings, designed to eliminatepigment separationandbatch inconsistencyissues throughoptimiz... |
 |
Valve Powder Coating | Characteristics of Valves Valves typically have the following characteristics: Thick and uneven walls Irregular shapes Rough surfaces High the... |