Electrostatic blue Polyester wrinkle Powder coating
Applications
-
Applied by electrostatic spraying gun that can provide negative tension of 60-80 kV.
-
Curing schedule : 180-200ºC /10-15 minutes depending on the powder chemistry.
-
Optimal film thickness : 80 -110 um.
-
The size of wrinkle pattern obtained depends on the coating thickness.
-
Excessively thin or thick films will not give a satisfactory finish.
Average Coverage
7-10m³/kg, the membrane is 60μm
(calculate by 100% utilization rate of powder coating).
Storage Requirements
Store below 30 °C, ventilated, dry, clean room, not near the fire, heat, direct sunlight, open dumps is prohibited.Under this condition, the powder can be stable for 12 months, more than the storage period may be re-examined, such as the results meet the requirements, can still be used.
Health and Safety
This product is non-toxic. In the course of inhalation of dust should be avoided. The operators should wear appropriate dust mask and glasses.
Specifications
| Chemistry Property | Inspection Standards | Test Indicators (High light) | Test Indicators (Glazed/Matte/Low light) |
|---|---|---|---|
| Impact resistance | ISO 6272, GB/T 1732-1993 | 50kg/cm | 40kg/cm |
| Cupping test | ISO 1520, GB/T 9753-1988 | 8mm | 7mm |
| The adhesion (grid method) | ISO 2409, GB/T 9286-1998 | 0 | 0 |
| Bending | ISO 1519, GB/T 6742-1986 | 2mm | 3mm |
| Pencil Hardness | ASTM D3363, GB/T 6739-1996 | 1H-2H | 1H-2H |
| Salt spray test | ISO 7253, GB/T 1771-1991 | >500 hours | >500 hours |
| Damp heat test | ISO 6270, GB/T 1740-1979 | >1000 hours | >1000 hours |
| Heat resistance | 110℃/24 hours (white) | Good gloss retention, ΔE≤0.3-0.4 | Good gloss retention, ΔE≤0.3-0.4 |
| Florida weathering exposure | ISO 2810, South 45°, 12 months | Gloss retention≥50% | Gloss retention≥50% |
| Artificial accelerated aging | 60℃/8 hours + 50℃/4 hours condensing, cycle for 500 hours | Gloss retention≥50%, Color stability: ΔE≤0.35 | Gloss retention≥50%, Color stability: ΔE≤0.35 |
| Annotate | 1. The above experiment uses 0.8mm steel with degreasing and rust removal, and the coating thickness is 50–70 microns.2. The above coating performance may be lower for glossy and slightly lower gloss finishes. |
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Polyester based powder coatin MT-MA200G White | Product Description MT-MA200G is a polyester based powder coating, formulated without TGIC and is designed for exterior exposure offering excellen... |
 |
Bonded Metal Powder Coatings for Pipes and Valves | Bonded metal powder coatings for pipes and valves are specialized coatings designed to provide both aesthetic appeal and functional protection to m... |
 |
Polyvinyl acetate powder coating | Brief description It is made of German and multi-head trees and chemicals such as TGIC or HAA. Features Excellent mechanical properties and exce... |
 |
Nitrobenzene | Introduction ItemsSpecificationDetection result Appearance Light yellow liquid Light yellow liquid Nitrobenzene content % > ... |
 |
Silk Textured Series Powder Coatings/powder coating brands | Silk Textured Powder Coating CategoryApplicationsPurposeKey Advantages Appliance Coating Refrigerators, washing machines, microwaves ... |