Instructions of Epoxy Zinc-Rich Primer
It is two components epoxy zinc-rich primer heavy corrosion by a zinc primer, epoxy resin and other components. On steel surface treated to form a hard, wear-resistant, durable film, and provide long-lasting cathode protection.
Property of Zinc Rich Primer Paint
Application of The zinc primer spray paint
Widely applicable to long-term anti-rust primer for steel primer, primer and maintenance, ships, bridges and other steel structures. Especially suitable for industrial, chemical, steel and other heavy-duty offshore matching primer coating.
Surface Preparation of The Epoxy Zinc-Rich Prime
The surface roughness of steel welds, rounded edges and clear the splash-melt welding, cleared the surface of the grease, oil and other pollutants; surface sandblasted to ISO standard Sa2.5 level or power tools rust St3 level; surface roughness of 50-85um, before spraying to ensure the surface is dry and clean.
The weather is good, the substrate temperature of not less than 5 ℃, relative humidity <85%. It must have good ventilation conditions in confined areas to ensure proper drying of the film. Before fully cured coating should not be exposed to oil, chemicals or mechanical stress.
Coating Application of Zinc Rich Epoxy Paint
Mixing mass ratio: Base material (A): The curing agent (B) = 10: 1.
Theoretical amount: 220 g / m2.
Painting passes: spraying or brushing 2 to 3, 60 to 80 microns dry.
Mixing: Use a power mixer component A (base) Stir, then stirring state by mixing ratio of the added amount of group B (curing agent), and fully mixed, while stirring continued momentum needed painting.
Thinner or Cleaner: For supporting diluent.
Curing time: After mixed directly.
After mixing pot life: 5 hours (23 ℃).
The Construction Method of Epoxy Zinc-Rich Prime
Brush: Recommended for small areas, acute sites and pre-coated and refinishing, but must meet the specified dry film thickness.
Spraying: airless spray or air spray, the airless spray is recommended priority.
Air spray: a discharge pressure 0.4-0.7Mpa, nozzle diameter 1.8-2.2mm;
Airless Spray: discharge pressure 15Mpa, nozzle diameter 0.43-0.48mm;
* When used in spray paint, because the need to adjust the viscosity, can be added to a thinner 0-10%.
Precautions
Shelf Life of The Epoxy Zinc-Rich Prime
Twelve months from the date of manufacture in the original unopened container at 32°C. Subject to re-inspection thereafter. Store in dry, shaded conditions away from sources of heat or ignition.
Package: 20 kg/ barrel.
Contact us get more details about Epoxy Zinc-Rich Primer Coating, such as TDS, Application Method, OEM etc.
Technical Data of The Epoxy Zinc-Rich Prime
|
UNCURED |
|
|
Appearance |
Thick paint |
|
Viscosity |
1700-2200 cP |
|
Cure System |
The catalyst cure |
|
Table Dry |
|
|
CURED At standard conditions (25℃and 50% relative humidity) for 5 days |
|
|
Hardness |
H ( pencil hardness) |
|
Color |
Colored |
|
Gloss |
Flat-high light |
|
Adhesion |
1 |
Fujian RuiSenNew Materials Co., Ltd. was established in 2007, located in Fujian Province, China. RuiSen is the largest manufacturer of RTV Silicon Coating (HVICs) in China, has many years' experience about R&D, manufacture management, and project management. We are the high-tech public company in China that specializes in Research and Development, Design, Manufacture, Sales and Project construction.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Enhanced Anti-pollution Flashover Coating RTV-II | We offer different kinds of Station Post Insulator for Substation, Line Post Insulator, Disc Suspension Insulator, Hollow & Bushing Insulator, ... |
 |
Line Post Insulator | We can offer different Voltage of Line Post Insulatorfor Transmission Line. Such as Long Rod Insulator, Rod Insulator and Pin Type Insulator. Cont... |
 |
Instructions of Epoxy Zinc-Rich Primer | It is two components epoxy zinc-rich primer heavy corrosion by zinc primer paint, epoxy resin and other components. On steel surface treated to for... |
 |
Hollow & Bushing Insulator | Fujian RuiSenNew Materials Co., Ltd. was established in 2007, located in Fujian Province, China. RuiSen is the largest manufacturer of RTV Silicone... |
 |
Busbar Insulation Coating | The silicone rubber insulation coating is made from special silicone rubber, high-performance material and other polymers by polymer blending techn... |
Похожие товары
 |
LC12 Two-Component Solvent Free Silicone Conformal Coating | Продавец: Nanjing Silfluo New Material Co., Ltd. | Conformal Coating, also called silicone coating pcbelectronic circuit board protection oil, coati... |
 |
LA-17 Polyether Modified Short Chain Polysiloxane | Продавец: Nanjing Silfluo New Material Co., Ltd. | Polyether modified trisiloxaneshort chain polysiloxane. Compared to trisiloxane surfactant,it has... |
 |
LA-14 A Modified Trisiloxane and an Silicone Surfactant | Продавец: Nanjing Silfluo New Material Co., Ltd. | (It is a substitution of Silwet ECOand Xiameter(R) OFX-0309) A modified Trisiloxane and an silico... |
 |
LA-11 A Modified Trisiloxane and an Silicone Surfactant | Продавец: Nanjing Silfluo New Material Co., Ltd. | (It is a substitution of silwet l 77) A modified Trisiloxane and an silicone surfactant with supe... |
 |
KSS Potassium Diphenylsulfone Sulfonate | Продавец: Nanjing Silfluo New Material Co., Ltd. | KSS is a high heat stable PC additive. Equivalents to FR2025, EF-42. Description of KSS Potass... |