Polyester based powder coating
Product Description
MT-OA110G is a polyester based powder coating, formulated without TGIC.
Powder Properties
| Chemical type | Polyester TGIC-free |
| Appearance | Smooth Matt |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.53-1.63 g/cm³ |
| Film Thickness | 75 – 100 microns |
| Coverage | 7.8 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
|
Stoving schedule (object temperature) |
10 minutes @ 200°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Gold Seal polished steel |
| Pretreatment | Lightweight Zinc phosphate |
| Film Thickness | 70 – 80 microns |
| Stoving Schedule | 10 minutes at 200°C |
Mechanical Tests
| test | results | |
| Flexibility | ISO6860 | 5mm |
| Erichsen cupping | ISO1520 | 6mm |
| Adhesion | ISO2409 | 100% |
| Impact (dir/rev) | ISO 6272 | 30/30 kgcm |
| Gloss(@60°） | ISO 2813 | 30±5% |
| Hardness(Buchholz) | ISO2815 | 8-125 |
| Reflectance Class | DIN EN 16268 | A |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-OA110G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-OA110G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
4-acryloylmorpholine CAS 5117-12-4 | Introduction CAS NO. 5117-12-4Molecular formula: C7H11NOAppearance: Colorless or pale yellow transparent liquidContent: 98%minColor code: 30APHA m... |
 |
Styrene CAS 100-42-5 | Introduction Styrene SDEB is a type of styrene produced by catalytic dehydrogenation of ethylbenzene. It is used to manufacture polystyrene, A... |
 |
Composite materials – modified silane sealant | MT-667is a single component sealant based on silane modified polymer, which solidifies into an elastomer by reacting with moisture and has good adh... |
 |
hydroxyfunctional polyacrylic dispersion (MT-A-145) | Introduction Characterization MT-A-145 is a water-reducible, hydroxyfunctional polyacrylic dispersion.It is suitable for use in combination w... |
 |
Indanthrone Blue CAS 81-77-6 | Introduction TestItem Specification Contofwater%≤ 2.5 Soluble matter in water %≤ 2.0 O... |
Похожие товары
 |
Epoxy/Polyester Powder Coatings | Продавец: Standard International Group (HK) Limited | Feature: -Good bond ability and mechanical performance -Smooth and glossy -Certified chemical ... |
 |
Polyester Clear Powder Coatings | Продавец: Standard International Group (HK) Limited | This series of product are made of polyester resin (as hardener) and highly transparentmaterials.... |
 |
Acrylic Clear Powder Coatings | Продавец: Standard International Group (HK) Limited | Feature: -Excellent exterior exposure durability -Excellent durable high gloss -Excellent clar... |
 |
Polyurethane Powder Coatings | Продавец: Standard International Group (HK) Limited | Feature： -Excellent exterior exposure durability -Good flowing -Excellent chemical resistance ... |
 |
MDF Powder Coating | Продавец: Standard International Group (HK) Limited | Feature： -Environmental friendly -No solvents and volatile organic compounds involved which are... |