Forged Entire CNC Machined Pelton Runner
Forged Entire CNC Machined Pelton Runner
Forging could considerably improve metal's organizational structure and mechanical property.
Forging offers uniformity of composition and structure. Forging results in metallurgical recrystalisation and grain refinement as a result of the thermal cycle and deformation process. This strengthens the resulting steel product particularly in terms of impact and shear strength.Forged steel is generally stronger and more reliable than castingspart.
Project Basic Information
Project Name: Minas-San Francisco HPP
Project Location: Ecuador
Pelton runner pitch diameter: 2460mm.
OD: 3179mm
Net Weight: 13300KG
Buckent No. 21
Output: 91.6MW
Product Introduction
Forging could considerably improve metal’s organizational structure and mechanical property.
Forging offers uniformity of composition and structure. Forging results in metallurgical recrystalisation and grain refinement as a result of the thermal cycle and deformation process. This strengthens the resulting steel product particularly in terms of impact and shear strength.
Forged steel is generally stronger and more reliable than castings of same material due to the fact that the grain flows of the steelare altered, conforming to the shape of the part.
Getai Hydropower is Pelton Turbine Experiment, Francis Turbine Diagram, Francis Turbine Working, Pelton Turbine For Salefactoty.
Performancecomparison table of forging parts and casting parts
Performance test of forging part
|
Mechanical Property |
σb（Mpa） |
σ0.2（Mpa） |
δ5（%） |
ψ（%） |
AKV（J/cm²） |
HB |
|||||
|
Standard value |
≥795 |
≥620 |
≥15 |
≥45 |
≥50 |
230～295 |
|||||
|
Actual value |
Horizontal |
815 |
655 |
107 |
102 |
110 |
259 |
256 |
253 |
||
|
Vertical |
820 |
660 |
67 |
149 |
152 |
136 |
256 |
257 |
257 |
||
Performance test of casting part
|
Mechanical Property |
σb（Mpa） |
σ0.2（Mpa） |
δ5（%） |
ψ（%） |
AKV（J/cm²） |
HB |
||||
|
Standard value |
≥750 |
≥550 |
≥15 |
≥35 |
≥50 |
221～286 |
||||
|
Actual value |
770 |
610 |
17 |
50 |
84 |
88 |
85 |
252 |
255 |
254 |
- Machining vedio for the Forged entire CNC machinedPeltonrunner.
More information please view here.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Francis Turbine Generator | Francis Turbine Generator Francis turbines are built in a compact structure, with high efficiency, and can be applied to a wide range of water hea... |
 |
Forged Entire CNC Machined Francis Runner | Forged Entire CNC Machined Francis Runner Forging could considerably improve metal’s organizational structure and mechanical property. For... |
 |
Double Francis Turbine | Double Francis Turbine The keyDoubleFrancis turbine components includes Runner, Distributor, Main shaft, Main shaft seal, Turbine guide bearing, G... |
 |
Francis turbine | Francis turbine Francis turbines are built in a compact structure, with high efficiency, and can be applied to a wide range of water heads. This f... |
 |
Forged Entire CNC Machined Pelton Runner | Forged Entire CNC Machined Pelton Runner Forging could considerably improve metal's organizational structure and mechanical property. Forging of... |
Похожие товары
 |
Аспарагиназа | Продавец: Компания BIT Bio-harbor | Аспарагиназа (ASN) — это амидная гидролаза, специфически катализирующая гидролиз аспарагина... |
 |
Ацетилестераза | Продавец: Компания BIT Bio-harbor | Ацетилэстеразы — это класс ферментов, специализированных на расщеплении ацетилэфирных связе... |
 |
β-N-Ацетилглюкозаминидаза | Продавец: Компания BIT Bio-harbor | β-Н-ацетилглюкозаминаза — это лизосомальный фермент, используемый для гидролиза n-ацет... |
 |
Хитиназа | Продавец: Компания BIT Bio-harbor | Хитиназа — это эффективный внеклеточный ферментный комплекс для расщепления хитина, получен... |
 |
ТЕВ протеаза | Продавец: Компания BIT Bio-harbor | ТЕВ-протеаза (протеаза вируса табачного травления) — это широко применяемое ферментное сред... |