ZG-P-7165/ZG-I-724
ZG-P-7165/ZG-I-7249,Poly ISO For Shoe Sole,High Density Low Hardness Sole Pu
Poly ISO For Shoe Sole
High Density Low Hardness Sole Pu
Medium and low-hardness and medium and low-density PU Resin for sole of casual shoes for both men and women
Characteristic: Medium and low hardness, medium and low density.
Application: Applicable to the production of medium soles of casual shoes for both men and women
Typical properties of PU Resin
|
Name of products |
Appearance |
Viscosity（Pa·s/50℃） |
Density（g/cm3/40℃） |
Package（kg） |
|
ZG-P-7165 |
White or pale yellow, liquid, no foreign material |
18 |
||
|
ZG-I-7249 |
Transparent liquid, no foreign material |
20 |
Reference shipments ratio: A/B=30/23(barrel)
Catalysts and auxiliary agents:
ZG-P-7165/ZG-AC-2/water=18kg/220g/60-80g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Poly Isocyanate PrepolymerMolding conditions & physical properties:
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratioP+C/I |
100/87-89 |
Molded density of sole（g/cm3） |
|
|
Using temperature（℃） |
material: 45-50; B material:38-42 |
Hardness (type A) |
40~55 |
|
Cream time（s） |
6~9 |
Tensile strength（MPa） |
|
|
Rise time（s） |
30~45 |
Elongation（％） |
350~450 |
|
Metal mold temperature（℃） |
55~65 |
NBS abrasion resistance（％） |
≥10% |
|
Demould time（min） |
Free foam density（g/cm3） |
||
|
Folding endurance (room temperature)(40,000 gap length mm) |
＜8 |
Polyurethane Resin For Shoe Sole
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
ZG-P-6570H/ZG-I-7118 | ZG-P-6570H/ZG-I-7118,, PU Resin for shoe sole with the upper Characteristic: Medium and low hardness, medium and high density Application: Applic... |
 |
ZG-P-6570/ZG-I-5012 | ZG-P-6570/ZG-I-5012 Dual density PU Resin for labor protection shoes (safety shoe) sole Characteristic: Medium and low hardness, medium and high ... |
 |
ZG-P-6955 / ZG-I-8308 | Low-hardness and medium-density shoe sole PU Resin for casual shoes for both men and women Characteristic: Low hardness, medium density. Ap... |
 |
High Density Upper Sole PU Resin | ZG-P-8755/ZG-I-7118 Q/ZHTY 01—2013 Application: Low hardness, high density. Characteristic: Suitable for shoes production. Typical properti... |
 |
ZG-P-5090/ZG-I-5320 | ZG-P-5090/ZG-I-5320 High-hardness and medium and high-density PU Resin for shoe sole of woman high-heeled shoes Characteristic: High hardness, me... |