ZG-P-8130/ZG-I-8260
ZG-P-8130/ZG-I-8260,,
PU Resin for shoe sole of cold-resistant shoes
Characteristic: Medium hardness, medium and low density, cold resistance and semi cold resistance
Application: Applicable to the production of cold-resistant and half hardy soles for both men and women shoes
Typical properties of
|
Name of products |
Appearance |
Viscosity（Pa·s/50℃） |
Density（g/cm3/40℃） |
Package（kg） |
|
ZG-P-8130 |
White or pale yellow, liquid, no foreign material |
18 |
||
|
ZG-I-8260 |
Transparent liquid, no foreign materials |
20 |
Reference shipments ratio: A/B=30/24(barrel)
Catalysts and auxiliary agents:
ZG-P-8130/ZG-AC-2/water =18kg/220g/0-30g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratioP+C/I |
100/80-82 |
Molded density of sole（g/cm3） |
|
|
Using temperature（℃） |
material: 45-50; B material:38-42 |
Hardness (type A) |
45~55 |
|
Cream time（s） |
7~9 |
Tensile strength（MPa） |
|
|
Rise time（s） |
30~45 |
Elongation（％） |
350~450 |
|
Metal mold temperature（℃） |
45~55 |
NBS abrasion resistance （％） |
≥10% |
|
Demould time（min） |
Free foam density（g/cm3） |
||
|
Folding endurance (room temperature)(40,000 gap length mm) |
＜8 |
Molding conditions & physical properties:
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
More information can view .
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
ZG-P-8130/ZG-I-8260 | ZG-P-8130/ZG-I-8260 PU Resin for shoe sole of cold-resistant shoes Characteristic: Medium hardness, medium and low density, cold resistance and s... |
 |
Sandals Shoes Sole PU Resin | Medium and high-density PU Resin for shoe sole with the upper Characteristic: Medium and low hardness, medium density and feel good Applica... |
 |
ZG-P-6955 / ZG-I-8308 | ZG-P-6955 / ZG-I-8308,PU Resin For Casual Shoes,High Density Low Hardness Sole Pu PU Resin For Casual Shoes High Density Low Hardness Sole Pu Low-h... |
 |
Low Hardness Sole PU Resin Supplier | PU Resin for Auto Parts Characteristic: Medium and low hardness, medium density Characteristic: Applicable to the production of related auto ... |
 |
ZG-P-8086/ZG-I-9823 | Super high-hardness and super low-density PU Resin for shoe sole Characteristic: Super-high hardness, super-low density. Application: Applica... |