Polyester based powder coating
Product Description
MT-OA110G is a polyester based powder coating, formulated without TGIC.
Powder Properties
| Chemical type | Polyester TGIC-free |
| Appearance | Smooth Matt |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.53-1.63 g/cm³ |
| Film Thickness | 75 – 100 microns |
| Coverage | 7.8 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
|
Stoving schedule (object temperature) |
10 minutes @ 200°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Gold Seal polished steel |
| Pretreatment | Lightweight Zinc phosphate |
| Film Thickness | 70 – 80 microns |
| Stoving Schedule | 10 minutes at 200°C |
Mechanical Tests
| test | results | |
| Flexibility | ISO6860 | 5mm |
| Erichsen cupping | ISO1520 | 6mm |
| Adhesion | ISO2409 | 100% |
| Impact (dir/rev) | ISO 6272 | 30/30 kgcm |
| Gloss(@60°） | ISO 2813 | 30±5% |
| Hardness(Buchholz) | ISO2815 | 8-125 |
| Reflectance Class | DIN EN 16268 | A |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-OA110G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-OA110G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
Send product request
Other supplier products
 |
CAS 1823-59-2 | Introduction 4.4 ‘-oxybis-phthalic anhydride is a white to white powder organic substance that can be used to make polyimide resins. Applic... |
 |
Composite Material – Acrylic Instant Drying Adhesive | MT941/MT912/MT994 series: One component quick curing, solvent-free cyanoacrylate adhesive. The product covers various specifications, strengths, c... |
 |
TBBS (NS) CAS 95-31-8 N-tert-butylbenzothiazole-2-sulphenamide | Introduction Chemical Name:N- tert- butyl- 2- benzothiazole sulfenamide CAS NO.:95-31-8 Product Specification: Appearance White or light... |
 |
Dimethyl Lauryl/myristyl Amine CAS 84649-84-3 | Introduction Chemical Name Dimethyl Lauryl/myristyl Amine Product Category Fatty Tertiary Amine CAS No. 84649-84-3 Content... |
 |
Methylated Urinary Aldehyde Resin | Methylated Urinary Aldehyde Resin: Properties and Applications Table 1: Key Characteristics of Methylated Urinary Aldehyde Resin PropertySpec... |
Same products
 |
Epoxy/Polyester Powder Coatings | Seller: Standard International Group (HK) Limited | Feature: -Good bond ability and mechanical performance -Smooth and glossy -Certified chemical ... |
 |
Polyester Clear Powder Coatings | Seller: Standard International Group (HK) Limited | This series of product are made of polyester resin (as hardener) and highly transparentmaterials.... |
 |
Acrylic Clear Powder Coatings | Seller: Standard International Group (HK) Limited | Feature: -Excellent exterior exposure durability -Excellent durable high gloss -Excellent clar... |
 |
Polyurethane Powder Coatings | Seller: Standard International Group (HK) Limited | Feature： -Excellent exterior exposure durability -Good flowing -Excellent chemical resistance ... |
 |
MDF Powder Coating | Seller: Standard International Group (HK) Limited | Feature： -Environmental friendly -No solvents and volatile organic compounds involved which are... |