CA Series-330CA30 PEEK Carbon Fiber Reinforcement
CA Series-330CA30cf peekcarbon fiber reinforcement is suitable for the production of bushing seals and other products, can be faster from the bearing surface heat dissipation, at the same time has a high thermal deformation temperature (336 ° C) , also can maintain strength at high temperature, to a certain extent, can replace metal materials.
Specification of CA Series-330CA30 PEEK Carbon Fiber Reinforcement
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
|||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
℃ |
343 |
|
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
|
Amorphous |
gcm-3 |
|||
|
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
|
by immersion |
Equilib riu m,23℃ |
% |
||
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
|
23℃,50kHz |
3 |
|||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
Ω cm |
10 9 |
||
As one of peek suppliers, we can offer kinds of peek plastic materialfor sale, anything you need, please contact us.
在线联系供应商
Other supplier products
 |
CA Series-770CA30 PEEK Carbon Fiber Reinforcement | CA Series-770CA30 carbon fiber filled PEEKreinforcement is widely used in automobile and aviation fields. It is widely used in automobile fuel pump... |
 |
Grade GL Glass Filled Fiber Reinforced PEEK | PEEK-GL series, is a glass fiber composite modified peek plastic materials, currently available from 5% -35% of different mass fractions of reinfor... |
 |
PEEK in Wires & Cables | Polyetheretherketone PEEKhas outstanding heat aging properties, good flame retardancy, self-extinguishing, hydrolysis resistance, corrosion resista... |
 |
Grade FC Super Wear Resistant PEEK | PEEK-FC series modified by PTFE, graphite and carbon fiber have lower friction coefficient, wear resistance and self-lubrication than pure resin G.... |
 |
Polyetheretherketone (Peek) for Medical Applications | Polyetheretherketone PEEKfor Medical Applications PEEKmedical gradehas good biocompatibility, non-toxicity, low density, and excellent mechanica... |
Same products
 |
FT wax used for EVA-based hot melt adhesive | 卖方: Syntop chemical Co.,Ltd. | Fischer-Tropsch wax is a commonly used performance modifier in hot melt adhesives, especially for... |
 |
high melting point FT wax improve the heat resistance of adhesives | 卖方: Syntop chemical Co.,Ltd. | FischerTropsch wax is an alkane polymer produced from synthesis gas or natural gas via the Fische... |
 |
For hot melt adhesive high melting point FT WAX | 卖方: Syntop chemical Co.,Ltd. | The key advantage of high-melting-point Fischer-Tropsch wax in hot-melt adhesives stems from its ... |
 |
Diesel Injection Delivery Valve 1W6982 | 卖方: China lutong | Diesel Injection Delivery Valve 1W6982 Diesel Injection Delivery Valve 19AChris Diesel Injection... |
 |
High melting point FT wax used as plastic processing additives | 卖方: Syntop chemical Co.,Ltd. | Due to its high purity, low oil content, narrow melting range, high hardness, and excellent therm... |