Color PEEK R&D Series
PEEK ColorR&D Series can be customized according to the customer's own demand. Different PEEK plastic colorscan be chosen for our PEEK raw material. Having good thermal stability, color consistency, high purity, and high-temperature resistance, our PEEK material colorR&D series is just as high quality as other naturalPEEK materialseries.
PEEK Material Color R&D Series Specifications
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
|||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
℃ |
343 |
|
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
|
Amorphous |
gcm-3 |
|||
|
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
|
by immersion |
Equilib riu m,23℃ |
% |
||
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
|
23℃,50kHz |
3 |
|||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
Ω cm |
10 9 |
||
More types of peek composite material, please visit our website.
在线联系供应商
Other supplier products
 |
Grade CA Carbon Fiber Reinforcement PEEK | PEEK-CA series reinforced plastics filled with carbon fiber, high elastic modulus, mechanical strength, creep resistance, wear resistance and dynam... |
 |
Grade GL Glass Filled Fiber Reinforced PEEK | PEEK-GL series, is a glass fiber composite modified natural PEEKmaterials, currently available from 5% -35% of different mass fractions of reinforc... |
 |
Peek in Bearing Material | Peek in Bearing Material Due to its excellent mechanical strength, dynamic fatigue resistance, high-temperature resistance, creep resistance, se... |
 |
Grade CA Carbon Fiber Reinforcement PEEK | PEEK-CA series reinforced plastics filled with carbon fiber, high elastic modulus, mechanical strength, creep resistance, wear resistance and dynam... |
 |
Grade CA Carbon Fiber Reinforcement PEEK | PEEK-CA series reinforced plastics filled with carbon fiber, high elastic modulus, mechanical strength, creep resistance, wear resistance and dynam... |
Same products
|
|
Color PEEK R&D Series | 卖方: Jilin Joinature Polymer Co.,Ltd. | PEEK ColorR&D Series can be customized according to the customer's own demand. Different PEEK... |