PA6 GF30 Halogen-free FR (A1015F) for Engineering Plastics
PA6 FRis a PA6 with 30% glass-fibers and flame retardant free of halogens.
Typical Application of PA6 GF30 halogen-free FR (A1015F)
PA6 GF30flame retardant free of halogens has achieved full coverage from electronic&electrical fields to the industrial, commodity consumer market, and even the automotive industry. Such as MCB panel (v0), power tool housing (HB), small household appliance accessories for bread machine housing and vacuum cleaner accessories (HB), and daily necessities structural parts-office chair legs (HB) and exhaust duct (HB), etc.
Processing Detail of PA6 GF30 halogen-free FR (A1015F)
Other Details of PA6 GF30 halogen-free FR (A1015F)
Physical Property
|
Ash |
(15.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1250Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.5-0.7 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.7-1.1% I ISO294-4) |
Mechanical Properties
|
Tensile strength(125.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break(2.5% I ISO527) Conditioned |
|
|
Notched Impact Strength(125 0MPa I ISO527) Conditioned |
2mm/min |
|
Flexural Strength(190MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus(5700 MPa I ISO178) Conditioned |
5mm/ min |
Thermal Property
|
Melting Point |
(220°C I ISO11357) |
|
Hot Deformation Temperature |
(175*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
240-260°C |
|
Nozzle Temperature |
240-260*C |
|
Tooling Temperature |
80*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
If you are looking for a reliable modified plastics inc, don't hesitate to contact us!
在线联系供应商
Other supplier products
 |
PA66 GF45 (A2011I) | PA66 GF45is a 45% glass fiber reinforced polyamide 6.6 with high stiffness and strength. Typical Application of PA66 GF45(A2011I) PA66 45%GF HB... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | PA66 GF15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection molding. PA66 GF15 Storage and Handling PRE-PROCESS... |
 |
PA6 GF in Anmei | As anengineered plastics company, Anmei focuses on the production of modified engineering plastics, among which high-performance nylon 6 engineerin... |
 |
PA6 GF20 Heat Stabilized (A1006D, A1016D) for Engineering Plastics | PA6 GF 20has 20% glass fiber filler. It has much greater heat-resistant mechanical properties than unfilled polyamide. Anmeiplastics has always bee... |
 |
PA6 GF30 Heat Stabilized (A1006F, A1016F) for Engineering Plastics | AnmeiA1006F is a kind of material PA6 GF30, which is the injection grade resin by mixing the 30% glass fiber and heat stabilized polyamide 6. Typi... |
Same products
 |
COLMAST®CW1350（白色母粒） | 卖方: ADC PLASTIC., JSC | COLMAST CW1350因其突出的优点和与不同类型的初级塑料树脂（PP、PE、ABS...）的结合而成为完美的选择，白色母粒越来越广泛地应用于编织袋、塑料制品的注塑等。 .. 请访问我们的... |
 |
CALMAST®MN570 – PP碳酸钙填充母粒 | 卖方: ADC PLASTIC., JSC | CALMAST MN570 是帮助塑料制品制造商优化成本并提高机械和物理性能（例如耐热性、表面改善、提高成品的撕裂强度和拉伸强度）的完美选择。 特别是提高最终产品加工的稳定性。 请访问我们的网... |
 |
CALMAST®MF530 – PP碳酸钙填充母粒 | 卖方: ADC PLASTIC., JSC | CALMAST MF530 是帮助塑料产品制造商优化成本并提高机械和物理性能（例如耐热性、表面改善、提高成品的冲击强度和拉伸强度）的完美选择。 特别是提高最终产品加工的稳定性。 请访问我们的网... |
|
|
PA6 GF30 Halogen-free FR (A1015F) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | PA6 FRis a PA6 with 30% glass-fibers and flame retardant free of halogens. Typical Applicati... |
 |
PA6 GF30 Halogenated FR (A1014F) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | PA6 GF 30 FRis a PA6 with 30% glass-fibers and halogens flame retardant. PA6 GF30 Halogenated ... |