Foam Repeated Compression Tester

Whats/App: +86 156 1874 6768

Web: standard-groups.com

Foam repeated compression testing machine will accurately measure the thickness of the test piece, placed in the compression plate of the testing machine, at the rate of 60 times per minute, compress the specimen at the frequency of 60 times to compress the height of the specimen 50%, reciprocating compression up to 80.000 times, after 30 minutes at room temperature, measure its thickness to convert the compression deformation rate.

Applications

1. Applicable Foam Material Types

Polyethylene foam materials (corresponding standards: ISO 7214. JIS K6767)

Latex foam rubber cushioning materials (corresponding standard: JIS K6382)

Other flexible porous polymer foams (such as polyurethane soft foam, etc., adaptable to similar compression fatigue testing requirements)

2. Applicable Product Fields

Furniture industry: Foam cushions for sofas/chairs, backrest foam, mattress filling foam (testing for collapse and deformation after long-term use)

Automotive interior industry: Car seat cushioning foam, headrest foam, interior shock-absorbing foam (evaluating performance stability after repeated compression during driving)

Packaging industry: Foam materials for cushioning packaging (verifying protective capabilities after multiple compressions)

Daily necessities industry: Foam cushions, footrests, and other products (testing durability during daily use)

Standards

GB/T 40872-2021: Test Methods for Polyethylene Foams

ISO 7214:2007: Cellular plastics — Polyethylene — Test methods

JIS K6382: Test Method for Repeated Compression of Rubber Materials

GB/T 42258-2022: Determination of Fatigue Properties of Flexible Porous Polymer Materials by Constant Deformation Method

JIS K6767-1999: Test Methods for Polyethylene Foams and Cellular Rubber Materials

Features

1. Standardized Testing Functions and Procedures

The system simulates the repeated compression conditions of foam materials in actual use. The sample is compressed to 50% of its initial height at a frequency of 60 cycles/minute, allowing for up to 80.000 cycles of reciprocating compression.

After testing, the sample is left to rest at room temperature for 30 minutes before precisely measuring its thickness and calculating the compression deformation rate. The process conforms to professional testing standards and effectively evaluates the fatigue resistance of the foam. The system possesses precise sample thickness measurement capabilities, providing fundamental support for the accuracy of the test data.

2. Multi-Standard Compatibility

Compliant with international standard ISO 7214 (Test Methods for Polyethylene Foam Materials), Japanese Industrial Standard JIS K6767 (Polyethylene Foam Testing), and JIS K6382 (Latex Foam Rubber Cushioning Material Testing), it meets the compliance testing needs of different types of foam materials.

3. Flexible Technical Adaptability

The compression stroke covers 0-50mm, adaptable to foam samples of various thicknesses (such as common 20-50mm thick samples). Equipped with a stable operating system (such as a motor and LCD counter), it supports high-cycle (up to 80.000 cycles) continuous reciprocating compression. The testing process does not require long-term personnel supervision, and the system automatically stops after reaching the set number of cycles.

Technical Parameters

Parameter	Specification
Meet the standard	ISO-7214. JIS-K6767. K6382
Compression stroke	0——50mm
Compression rate	60 cpm (cycles per minute; noted: original shows "60cm", likely a typo)
Pressure plate spacing	200mm
Test size	200×200mm
Plate area	30×30cm
Upper pressure plate	V-type exhaust trench distance: 19×19mm
Lower pressure disc	289 air holes, hole distance: 19mm
Motor	1/3HP
Counter	LCD, 0——999999
Volume	60×40×75cm
Weight	102kg
Power Supply	1 # AC 220V, 5A (noted: original shows "AC220. 5A", corrected for clarity)

Other supplier products

	Goggles Puncture Resistance Testing Machine	Whats/App: +86 156 1874 6768 Web: standard-groups.com The safety goggle puncture resistance testing machine is a device used to test the puncture...
	Carbon black dispersion instrument for global buyers	Get a quote： Whats/App: +86 156 1874 6768 Web: standard-groups.com Application DW1431 plastic carbon black dispersion measurement system is bas...
	Metal Wire Wrap Tester	Whats/App: +86 156 1874 6768 Web: standard-groups.com According to the criteria: GB/T 2976 "Wire winding test method for Metal Materials" ISO 4...
	Film Impact Testing Apparatus (Gardner Type)	Whats/App: +86 156 1874 6768 Web: standard-groups.com Product Introduction: The coating impact resistance test device is mainly used to test the...
	ISO 7148 Heavy-Duty Reciprocating Friction and Wear Testing Machine Supplier	Get a quote： Whats/App: +86 156 1874 6768 Web: standard-groups.com The Heavy-Duty Reciprocating Friction and Wear Testing Machine is a high-perf...

All supplier products

Same products

	HDPE High Speed Water Cooled Double Wall Corrugated Pipe Extrusion Line	Seller: Shandong HUASU Plastic Technology Co.,Ltd.	The molds adopt the double flow channel structure and nitriding polishing processed die head. Thi...
	PanEVAP & MVR system	Seller: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd	A multiple-effect evaporator is a device that efficiently uses steam heat to evaporate water. Wat...
	PanGAP wide gap welded plate heat exchanger	Seller: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd	PanGAP wide gap welded plate heat exchangerconsists of a welded plate pack with different channel...
	PanBloc welded plate heat exchanger	Seller: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd	PanBloc welded plate heat exchangeris compact and efficient, although fully welded, is totally ac...
	PanBox welded plate heat exchanger	Seller: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd	PanBox welded plate heat exchangerconsists of a laser welded plate pack with optimized corrugated...