Low Temperature-resistance TPO
The modification of ATP for polyolefin elastomers mainly reflects the following technical characteristics:
In the application of cable insulant, the modification TPO of ATP can not only meet the requirement of electric performance from the insulant but also display a more broad temperature resistant character——displaying excellent mechanical properties and aging properties at the test temperature of -50℃—+125℃. So, this is the optimized insulant for wires and cables which have special requirements for low-temperature resistance.
The jacket made up of TPO wire and cable insulant from ATP keeps its section surface smooth and orderly with little retraction rate after immersing in solder machine （350℃/2”）. In the application of high-temperature-resistant cables (temperature≤125℃) such as charging vehicle cables (EV Cable), equipment connection cables, etc., the jacket made up of TPO wire and cable insulant from ATP takes the place of XLPE materials to meet the requirements of insulant high-temperature aging and shrinkage for nominal cables. And this can simplify the processing procedures by a large margin and improve the processing efficiency and yield.
Application: TPO has the characteristics of small specific gravity, good impact strength, and low-temperature brittleness, and is suitable for applications in the cable industry.
Technical Data of Low Temperature-resistance TPO
|
Technical Data Sheet |
Model |
||||
|
Material Properties |
Test Standard |
Test Condition |
Unit |
2895F-ESS-1008S |
|
|
General Characteristics |
Material Category |
- |
- |
- |
|
|
Appearance(Light/Semi-matte/Frosted) |
- |
- |
- |
||
|
Extrusion/Injection |
- |
- |
- |
||
|
Physical Characteristics |
Hardness |
ISO 48 |
15S |
Shore A |
97 |
|
Proportion |
ISO 1183 |
- |
g/cm³ |
||
|
Melt Index |
ISO 1133-1:2011 |
190℃/2.16kg |
g/10min |
||
|
Brittle Temperature |
ISO 812 |
- |
℃ |
||
|
Mechanical Properties |
Elongation |
ISO37:2017 |
200mm/min |
% |
590 |
|
Tensile Strength |
ISO37:2017 |
200mm/min |
Mpa |
||
|
Tearing Strength |
ISO34-1:2015 |
500mm/min |
KN/m |
||
|
Hot Air Aging |
Elongation Retention Rate |
ISO37:2017 |
- |
% |
|
|
Tensile Strength Retention Rate |
ISO37:2017 |
- |
% |
||
|
Electrical Performance |
Volume Resistivity |
ASTM D257 |
- |
Ohm-cm |
|
|
Permittivity |
ASTM D150 |
- |
- |
||
|
Combustion Performance |
Vertical Burning Test |
UL 94 |
- |
||
|
Oxygen Index |
ASTM D2863 |
- |
% |
||
|
Feature |
|||||
As one of the most professional polymer compounding companies, we provide polymer compound, tpo polyolefin, polymer thermoplastic, tpe elastomero termoplastico and etc. For more information, please feel free to contact us!
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Super Soft TPEs | The rubber-like functional group is introduced into the material, and when applied to the cable sheath, it has more excellent wear resistance and s... |
 |
LSZH Compound from ATPolymer | ATPmaterialstarts the LSZH compound( LSOH material) research and development for various applications such as Rail Transit, Architecture&Home D... |
 |
Anti-Mildew TPEs | Thermoplastic Polyether Ester ElastomerApplicable: most kinds of medical equipment and special equipment lines that have biocompatibility, microorg... |
 |
Extruding LSZH | Technical Data of Extruding Cat6 LSOH Technical Data Sheet Model Material Properties Test Standard Test Cond... |
 |
ATP For High Flame Retardant Cables | ATP is able to quickly provide customers with High Flame Retardant cables material solutions that fully comply with the major building directives, ... |