Electrostatic spray paint Red Polyester powder coating
Properties
highly decorative ripple-pattern finishes.
available in any of powder chemistry types e.g. epoxy, polyester , epoxy polyester and polyurethane .
High ability to hide substrate defects.
Application Schedule
Applied by electrostatic spraying gun that can provide negative tension of 60-80 kV.
Curing schedule : 180-200ºC /10-15 minutes depending on the powder chemistry.
Optimal film thickness : 80 -110 um.
The size of wrinkle pattern obtained depends on the coating thickness.
Excessively thin or thick films will not give a satisfactory finish.
Average Coverage
8-10m³/kg, the membrane is 60μm (calculate by 100% utilization rate of powder coating).
Storage Requirements
Store below 30 °C, ventilated, dry, clean room, not near the fire, heat, direct sunlight, open dumps is prohibited.Under this condition, the powder can be stable for 12 months, more than the storage period may be re-examined, such as the results meet the requirements, can still be used.
Health and Safety
This product is non-toxic. In the course of inhalation of dust should be avoided. The operators should wear appropriate dust mask and glasses.
Specifications
| Chemistry Property | Inspection Standards | Test Indicators (High light) | Test Indicators (Glazed/Matte/Low light) |
|---|---|---|---|
| Impact resistance | ISO 6272. GB/T 1732-1993 | 50kg/cm | 40kg/cm |
| Cupping test | ISO 1520. GB/T 9753-1988 | 8mm | 7mm |
| The adhesion (grid method) | ISO 2409. GB/T 9286-1998 | 0 | 0 |
| Bending | ISO 1519. GB/T 6742-1986 | 2mm | 3mm |
| Pencil Hardness | ASTM D3363. GB/T 6739-1996 | 1H-2H | 1H-2H |
| Salt spray test | ISO 7253. GB/T 1771-1991 | >500 hours | >500 hours |
| Damp heat test | ISO 6270. GB/T 1740-1979 | >1000 hours | >1000 hours |
| Heat resistance | 110℃/24 hours (white) | Good gloss retention, ΔE≤0.3-0.4 | Good gloss retention, ΔE≤0.3-0.4 |
| Florida weathering exposure | ISO 2810. South 45°, 12 months | Gloss retention≥50% | Gloss retention≥50% |
| Artificial accelerated aging | 60℃/8 hours + 50℃/4 hours condensing, cycle for 500 hours | Gloss retention≥50%, Color stability: ΔE≤0.35 | Gloss retention≥50%, Color stability: ΔE≤0.35 |
| Annotate | 1. The above experiment uses 0.8mm steel with degreasing and rust removal, and the coating thickness is 50–70 microns.2. The above coating performance may be lower for glossy and slightly lower gloss finishes. | — |
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Functional Powder Coatings for Industry | Introduction Our Functional Powder Coatings go beyond aesthetics—built to endure harsh environments, resist damage, and meet specific techni... |
 |
filter element powder Coating | Introduction Accurate selection of powder has always been a problem for the powder industry. To solve this problem, we name the powder according t... |
 |
Powder Coating For Imitation Wood Grain | Introduction With the improvement of people’s environmental awareness, coating applications are becoming increasingly popular, especially ar... |
 |
Polyurethane powder coating series | Made of hydroxy polyester resin and isocyanate curing agent as the main raw materials. Features: –Good adhesion, good mechanical properties... |
 |
Metallic flat matte MT-019/74639 | Introduction No. MT-019/74639 Color Gray Surface Metallic flat matte System Weather-resistant polyester Scope of... |