High Build Epoxy Zinc-rich Primer( CE certificate )
Thick build epoxy zinc-rich primer is an epoxy zinc-rich primer with thick coating properties.
The thickness of 70μm～80μm can be reached by airless spraying at one time. The ordinary ce primerdoes not have the performance of the thick coating, and one spray is about 40μm. If it is too thick, the performance of the paint film will decrease. Under the same film thickness, the anti-rust performance and mechanical properties of ordinary epoxy zinc-rich primer are better than thick-build epoxy zinc-rich primer with the same film thickness. Medium and low film thickness, use an ordinary epoxy zinc-rich primer. High film thickness, using thick-build epoxy zinc-rich primer can save a lot of construction costs. But it has higher requirements for spray machines.
Advantage of High Build Epoxy Zinc-rich Primer( CE certificate )
Good cathodic protection
Excellent anti-corrosion and abrasion resistance property, good high build applicability
Good weather resistance, fast drying
Good gas cutting and welding property
Good matching property with many kinds of subsequent coat
Good adhesion to steel surfaces
zinc rich primer specification( CE certificate )
|
Type |
Solvent |
||||
|
Solid Content |
86% |
||||
|
Mixing Ratio |
two components base : hardener=10:1 by weight |
||||
|
Dry Film Thickness |
50μm per coat |
||||
|
Specific Gravity |
|||||
|
Coverage Rate (Theoretical) |
|||||
|
Drying Time |
Temperature |
5℃ |
10℃ |
20℃ |
30℃ |
|
Dry to touch |
20mins |
20mins |
10mins |
5mins |
|
|
Dry Hard |
36hrs |
24hrs |
18hrs |
10hrs |
|
|
Package |
33kgs for one kit, part A 30kgs, part B 3kgs |
||||
How to apply the epoxy zinc rich primer to 80μm DFT in one time spray?
FUXI® high build epoxy zinc-rich primer can be sprayed to 80μm by high-pressure airless spray, without sag, greatly saving the construction time and related cost.
After the epoxy zinc-rich primer is left for a long time, if it is not stirred, there is a transparent oily resin on the surface of the barrel. Can such epoxy zinc-rich paint still be used?
After the epoxy zinc-rich primer is left for a long time, if it is not stirred, there is a transparent oily resin on the surface of the barrel. Can such epoxy zinc-rich paint still be used?
The epoxy zinc-rich primer contains more zinc dust and has a larger specific gravity. Therefore, it is prone to delamination during storage. Under normal circumstances, there will be a small amount of solvent on the surface after about a month. That is normal. As long as it is easy to stir, the coating application does not sag, and the performance meets the requirements, it can be used normally. However, if the stratification causes the zinc dust layer to be difficult to stir, and the construction is easy to sag, the quality of the zinc-rich primer is problematic and should not be used.
JINHAI, as an excellent industrial coating manufacturer, offers a wide range of interior wall paintfor you to choose from.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
FUXI ® ZINC-RICH PAINT | Zinc powder is the most important electrochemical antirust pigment. A primer made with a large amount of zinc powder is called a zinc-rich primer. ... |
 |
Epoxy Floor Sealing Primer | FUXI® epoxy floor primeris formulated with specially modified epoxy resin, solvents and additives. It has excellent permeability, sealing prope... |
 |
High Chlorinated Polyethylene Anticorrosive Intermediate Paint | High chlorinated polyethyleneanticorrosive Intermediate Paint is composed of high chlorinated polyethylene resin, anticorrosive pigments, additives... |
 |
Chlorinated Rubber Anticorrosive Primer (Iron Red) | Chlorinated Rubber Anticorrosive Primer (Iron Red) Chlorinated rubber anticorrosive primer is combined with a chlorinated rubber resin, curing age... |
 |
High-Build Modified Epoxy Anticorrosive Primer (Iron Red) | Acrylic polysiloxane paint is a high-performance, two-component, high-solids hybrid topcoat. It complies with all current VOC regulations, and does... |