Rose Red Glossy Powder Coating
Powder type
Epoxy, Epoxy-Polyester, Polyester, Polyurethane
Applications
Exterior Industrial, Specialized
Finish type
Smooth
Color standard: RAL
RAL colors: RAL Classic K7
RAL code: 3017
RAL name
Rose
Gloss
High Gloss / G70-95. Semi Gloss / G40-70
Storage
Keep in a dry cool area (max. 25°C, 60% RH)
Shelf life
12 months
Application Data & Recommendations
Application methods
Electrostatic spray
Recommended film thickness
60-90 microns (2.4-3.6 mils) for smooth surfaces, 70-100 microns (2.8-3.9 mils) for textured surfaces
Theoretical coverage
5-8 m²/kg (24-39 ft²/lb) at 70-100 microns (2.8-3.9 mils) for textured surfaces, 8-12 m²/kg (39-59 ft²/lb) at 60-90 microns (2.4-3.6 mils) for smooth surfaces
Cure schedule
10 minutes at 160°C, 180°C, 200°C metal temperature
If you're ready to take the next step or Request Free Samples, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Send product request
Other supplier products
 |
Polyester Epoxy Hybrid Powder Coating Series – Others | Introduction It is made of polyester resin and epoxy resin as the main base materials, and has the excellent decorative, mechanical properties and... |
 |
Matte powder coating | Introduction Matte powder coating is a specialized type of coating that provides a non-reflective, low-gloss finish. It is applied as a dry powder... |
 |
Process water corrosion inhibitor (amine neutralizer) STD-8S | STD-8S process water corrosion inhibitor (amine neutralizer) has multifunctional effects: it has both neutralization, film-forming and deoxidation ... |
 |
Silk Textured Series Powder Coatings | Introduction Silk Textured Powder Coating CategoryApplicationsPurposeKey Advantages Appliance Coating Refrigerators, washing machines... |
 |
High Adhesion Powder Coatings – Strong & Durable Coating Solution | High adhesion powder coatings offer superior bonding, often requiring minimal or no primer, and are essential for complex, hard-to-coat parts like ... |