Polyester based powder coatin MT-MA200G White
Product Description
MT-MA200G is a polyester based powder coating, formulated without TGIC and is designed for exterior exposure offering excellent light and weather resistance from a single coat finish.
Powder Properties
| Chemical type | Polyester TGIC-free |
| Appearance | Smooth Matt |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.62 ± 0.05 g/cm³ |
| Film Thickness | 100 – 125 microns |
| Coverage | 6.2 ㎡/kg @ 100 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
| Stoving schedule
(object temperature) |
20 – 25 minutes @ 175°C
15 – 20 minutes @ 190°C 10 – 15 minutes @ 205°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Cold Rolled Steel |
| Pretreatment | B1000 Iron phosphate |
| Film Thickness | 100 – 125 microns |
| Stoving Schedule | 15 minutes at 190°C |
Mechanical Tests
| test | results | |
| Flexibility | ASTM D522 | 3mm |
| Adhesion | ASTM D3359 | 100% |
| Impact (direct | ASTM D2794 | 10/5 kgcm |
| Gloss(@60°） | ISO 2813 | 7.0 – 11.0% |
| Hardness (scratch) | ASTM D3363 | 2H |
| Reflectance Class | DIN EN 16268 | A+ |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-MA200G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-MA200G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
If you're ready to take the next step, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Send product request
Other supplier products
 |
Metallic flat matte MT-629/94777 | Introduction No. MT-629/94777 Color Champagne gold Surface Metallic flat matte System Super weather-resistant polyest... |
 |
Ultra flat thin powder coating | Application areas: Aluminum doors and windows curtains, automotive field, household appliances More excellent performance Leveling flatness comp... |
 |
Flat matte MT-049/82008 | Introduction No. MT-049/82008 Color Matte black Surface Flat matte System Polyester/049 Scope of application Fu... |
 |
Rutile titanium dioxide STD-895 | Rutile titanium dioxide STD-895 is a coatings grade titanium dioxide pigment manufactured by the chloride process. It is recommended for a range of... |
 |
Sand grain matte MT-019/81036 | Introduction No. MT-019/81036 Color Black Surface Sand grain matte System Weather-resistant polyester Scope of appli... |
Same products
 |
Hot Melt Adhesive for Vacuum Insulation Panels | Seller: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Vacuum Insulation Panels Supply & Technical Support Capabilities ... |
 |
Hot Melt Adhesive for Packaging | Seller: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Packaging Bond Strength & Durability: Hot melt adhesives provide i... |
 |
Hot Melt Adhesive for Hygiene Products | Seller: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Hygiene Products refers to thermoplastic pressure‑sensitive adhesives ... |
 |
LSAW Steel Pipe & Tube | Seller: HEBEI TIRICO PIPELINE CO.,LTD | LSAW Steel Pipe & Tube , or Longitudinal Submerged Arc-Welding Pipe (also known as SAWL ... |
 |
Anti-Corrosion Steel Pipe & Tube | Seller: HEBEI TIRICO PIPELINE CO.,LTD | Anti-Corrosion Steel Pipe & Tube Anti-Corrosion Steel Pipe & Tube What Is an Anti... |