RAL6005/6018 green Polyester Powder coating
Application Schedule:
Applied by electrostatic spraying gun that can provide negative tension of 60-80 kV.
Curing schedule : 180-200ºC /10-15 minutes depending on the powder chemistry.
Optimal film thickness :
80 -110 um
The size of wrinkle pattern obtained depends on the coating thickness.
Excessively thin or thick films will not give a satisfactory finish.
Average Coverage:
7-10m³/kg, the membrane is 60μm (calculate by 100% utilization rate of powder coating).
Storage Requirements:
Store below 30 °C, ventilated, dry, clean room, not near the fire, heat, direct sunlight, open dumps is prohibited.Under this condition, the powder can be stable for 12 months, more than the storage period may be re-examined, such as the results meet the requirements, can still be used.
Health and Safety:
This product is non-toxic. In the course of inhalation of dust should be avoided. The operators should wear appropriate dust mask and glasses.
Coating Performance:
| Chemistry Property | Inspection Standards | Test Indicators (High light) | Test Indicators (Glazed/Matte/Low light) |
|---|---|---|---|
| Impact resistance | ISO 6272, GB/T 1732-1993 | 50kg/cm | 40kg/cm |
| Cupping test | ISO 1520, GB/T 9753-1988 | 8mm | 7mm |
| The adhesion (grid method) | ISO 2409, GB/T 9286-1998 | 0 | 0 |
| Bending | ISO 1519, GB/T 6742-1986 | 2mm | 3mm |
| Pencil Hardness | ASTM D3363, GB/T 6739-1996 | 1H-2H | 1H-2H |
| Salt spray test | ISO 7253, GB/T 1771-1991 | >500 hours | >500 hours |
| Damp heat test | ISO 6270, GB/T 1740-1979 | >1000 hours | >1000 hours |
| Heat resistance | 110℃/24 hours (white) | Good gloss retention, ΔE≤0.3-0.4 | Good gloss retention, ΔE≤0.3-0.4 |
| Florida weathering exposure | ISO 2810, South 45°, 12 months | Gloss retention≥50% | Gloss retention≥50% |
| Artificial accelerated aging | 60℃/8 hours + 50℃/4 hours condensing, cycle for 500 hours | Gloss retention≥50%, Color stability: ΔE≤0.35 | Gloss retention≥50%, Color stability: ΔE≤0.35 |
| Annotate | 1. The above experiment uses 0.8mm steel with degreasing and rust removal, and the coating thickness is 50–70 microns.2. The above coating performance may be lower for glossy and slightly lower gloss finishes. | — |
Types of powder coating
Powder coatings can be categorized by resin system (epoxy, polyester, hybrid, polyurethane), appearance (smooth, texture, hammer, metallic, pearlescent), or performance level (anti-corrosion, heat-resistant, UV-resistant, architectural grade, automotive grade).
Send product request
Other supplier products
 |
Black Wrinkle Color Powder Coating | Introduction As one of the most experienced powder coaters in the industry, Standard boasts a large and loyal clientele that spans a wide range of... |
 |
Red Color Matte Powder Coating | Powder type Epoxy-Polyester, Polyester Applications Exterior Industrial, Specialized Finish type Smooth Color standard: RAL RAL colors: RAL ... |
 |
Wood grain transfer powder coating | Surface Finish Options Overview Product introduction: Transfer powder coating can form various patterns or patterns on the coating on the subst... |
 |
Light pole powder/anti static powder coating | Introduction Accurate selection of powder has always been a problem for the powder industry. To solve this problem, we name the powder according t... |
 |
Polyester based powder coating MT-JA010G White | Product Description MT-JA010G is a polyester based powder coating, formulated using TGIC and is designed for exterior exposure offering excellent ... |