Resin-specific adsorption of gold
Indicator Parameter
Functional group -N+(CH3) 2H2O
Appearance Milky white opaque sphere
Finished form CLˉ
Moisture content % 45-55
Weight whole exchange capacity mmol/g ≥5.0
Volume whole exchange capacity mmol/ml ≥1.50
Wet density g/ml 1.05-1.1
Wet real density g/ml 0.68-0.75
Particle size range % (0.6-1.80mm)≥95%
Granularity （<0.6mm）≤1.0
Uniformity coefficient 1.5
Sphere rate after abrasion % ≥95%
Indicator Parameter
Regeneration concentration HCl:2-4%；/NaOH:2-4%
pH range 1-10
Highest use temperature℃ OH-100/Cl-40
Expansion rate (OHˉ→Clˉ)% ≤15-20%
Operational flow speed m/h 10-30
Desorption ： "Resin adsorption of gold thiourea with 9% + 3% sulfuric acid analysis, analytical dosage of 6-8 times the bed volume, contact time with Resin for 2h or more.
"
Regeneration process： Resin after resolution after washing, rinse with 2-3 times the bed volumeNaOH, about 1 hour, then rinse renewable HCl solution, the dosage is 2 times the bed volume, time is about 1.5h, washed clean and odor can be the last. (Regeneration concentration reference Reference of indicator)
Other supplier products
|
|
Polyether polyol |
Model Hydroxyl value Water content Acid value pH value Potassium Chromaticity Viscosity Degree of unsaturation
mgKOH/g ％ mgKOH/g mg/Kg APHA mPa.s/... |
|
|
Zinc phosphate |
Project Medicine raw material special-purpose Feed additive special-purpose Sweetening agent special-purpose Rubber special-purpose Paint special-p... |
|
|
Toluene-2,4-diisocyanate |
Test items Index
Isocyanate ％ ≥99.0
Saponifiable chlorine ％ ≤0.01
Chlorine ％ ≤0.04
Crystallizing point℃ ％ 5.0-6.5
Chromaticity （Hazen... |
|
|
Anhydrous Sodium Sulfite |
Test items Food-grade High-purity grade Industrial-grade
Sodium sulfite (Na2SO3) % ≥ 97 98 97
Iron Fe % ≤ 0.001 0.001 0.003
Free Alkali (N... |
|
|
Zinc sulfate |
Testing Items monohydrate heptahydrate
Appearance White powder --
Zinc Sulphate content % ≥ 96.09 99
Zn % ≥ 35 22.51
Pb % ≤ 0.001 0.00... |