Polyurethane based powder coating White
Product Description
MT-PA020G is a polyurethane based powder coating, formulated without TGIC and is designed for exterior exposure offering excellent light and weather resistance from a single coat finish.
Powder Properties
| Chemical type | Polyurethane |
| Appearance | Smooth Matt |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.74 ± 0.05 g/cm³ |
| Film Thickness | 75 – 100 microns |
| Coverage | 7.7 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
|
Stoving schedule (object temperature) |
15 – 20 minutes @ 205°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Cold Rolled Steel |
| Pretreatment | B1000 Iron phosphate |
| Film Thickness | 75 – 100 microns |
| Stoving Schedule | 15 minutes at 205°C |
Mechanical Tests
| test | results | |
| Flexibility | ASTM D522 | 12 mm |
| Adhesion | ASTM D3359 | 100% |
| Impact (direct) | ASTM D2794 | 60 kgcm |
| Gloss(@60°） | ISO 2813 | 85 ± 5 |
| Hardness(scratch) | ASTM D3363 | 2H |
| Reflectance Class | DIN EN 16268 | A |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-PA020G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-PA020G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
Send product request
Other supplier products
 |
polymeric isocyanate (MT-44V20) | Introduction General Properties and Applications MT44V20 is a liquid, dark brown polymeric isocyanate based on diphenylmethane-4,4′-dii... |
 |
Tricresyl phosphate (TCP) CAS 1330-78-5 | This product is a colorless or light yellow transparent oily liquid. Odorless, strong stability, not easily volatile, with good plasticizing flame ... |
 |
2K-MMA two-component acrylic adhesive | 2K-MMA two-component acrylic adhesive is a structural adhesive with fast curing speed, high bonding strength, good toughness, and good aging resist... |
 |
Thermal interface material | Thermal conductive sealant There are two types of thermal conductive joint fillers: silicon-based and non silicon. They are usually two-component ... |
 |
polymeric isocyanate (MT-44V20) | General Properties and Applications MT44V20 is a liquid, dark brown polymeric isocyanate based on diphenylmethane-4,4′-diisocyanate (MDI) wi... |
Same products
 |
Epoxy/Polyester Powder Coatings | Seller: Standard International Group (HK) Limited | Feature: -Good bond ability and mechanical performance -Smooth and glossy -Certified chemical ... |
 |
Polyester Clear Powder Coatings | Seller: Standard International Group (HK) Limited | This series of product are made of polyester resin (as hardener) and highly transparentmaterials.... |
 |
Acrylic Clear Powder Coatings | Seller: Standard International Group (HK) Limited | Feature: -Excellent exterior exposure durability -Excellent durable high gloss -Excellent clar... |
 |
Polyurethane Powder Coatings | Seller: Standard International Group (HK) Limited | Feature： -Excellent exterior exposure durability -Good flowing -Excellent chemical resistance ... |
 |
MDF Powder Coating | Seller: Standard International Group (HK) Limited | Feature： -Environmental friendly -No solvents and volatile organic compounds involved which are... |