Polyester based powder coating
Product Description
MT-OA010G is a polyester based powder coating, formulated without TGIC.
Powder Properties
| Chemical type | Polyester TGIC-free |
| Appearance | Smooth Gloss |
| Particle Size | Suitable for electrostatic spray |
| Specific gravity | 1.54-1.64 g/cm³ |
| Film Thickness | 75 – 100 microns |
| Coverage | 7.8 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| Shelf life | 12 months |
|
Stoving schedule (object temperature) |
10 minutes @ 200°C |
Test Conditions
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Substrate | Cold Rolled Steel |
| Pretreatment | Lightweight Zinc phosphate |
| Film Thickness | 70 – 80 microns |
| Stoving Schedule | 10 minutes at 200°C |
Mechanical Tests
| test | results | |
| Flexibility | ISO6860 | 5mm |
| Erichsen cupping | ISO1520 | 6mm |
| Adhesion | ISO2409 | 100% |
| Impact (dir/rev) | ISO 6272 | 30/30 kgcm |
| Gloss(@60°） | ISO 2813 | >90 |
| Hardness(Buchholz) | ISO2815 | >80 |
| Reflectance Class | DIN EN 16268 | A |
Pre-treatment
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-OA010G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Application
MT-OA010G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
Send product request
Other supplier products
 |
Rheology modifier STD-9010 | Composition: Polyurea mixture solution Appearance: yellow transparent solution Active ingredient: 50% Solvent: N-methylpyrrolidoneScope of Appli... |
 |
CAS 4415-87-6 | Introduction of the Polyimide Polyimide (sometimes abbreviated PI) is a polymer of imide monomers. Polyimides have been in mass production since 1... |
 |
Modified Silane Sealant | Introduction MT-667is a single component sealant based on silane modified polymer, which solidifies into an elastomer by reacting with moisture an... |
 |
MS modified silane sealant | Introduction Modified silane sealant, environmentally friendly, has a wide range of adhesive properties, no need for primer, UV protection, no sol... |
 |
CAS 3081-01-4 7PPD N-(1,4- Dimethylpentyl)-N’- phenyl-p-phenylenediamine | Introduction Chemical Name:N-(1,4- Dimethylpentyl)-N’- phenyl-p-phenylenediamine CAS NO.:3081-01-4 Product Specification: Appearanc... |
Same products
 |
Epoxy/Polyester Powder Coatings | Seller: Standard International Group (HK) Limited | Feature: -Good bond ability and mechanical performance -Smooth and glossy -Certified chemical ... |
 |
Polyester Clear Powder Coatings | Seller: Standard International Group (HK) Limited | This series of product are made of polyester resin (as hardener) and highly transparentmaterials.... |
 |
Acrylic Clear Powder Coatings | Seller: Standard International Group (HK) Limited | Feature: -Excellent exterior exposure durability -Excellent durable high gloss -Excellent clar... |
 |
Polyurethane Powder Coatings | Seller: Standard International Group (HK) Limited | Feature： -Excellent exterior exposure durability -Good flowing -Excellent chemical resistance ... |
 |
MDF Powder Coating | Seller: Standard International Group (HK) Limited | Feature： -Environmental friendly -No solvents and volatile organic compounds involved which are... |