Dense Fireclay and High Alumina Refractory Castable
Mark & model：Dense Fireclay and High Alumina Refractory Castable
Origin：Asia and Pacific AreaChina
Quality standard：International
Product profile:Dense Fireclay and High Alumina Refractory Castable
|
DENSE FIRECLAY AND HIGH ALUMINA REFRACTORY CASTABLE |
||||||||||||||
|
Classification |
FIRECLAY BONDED |
CEMENT BONDED |
LOW CEMENT BONDED |
PHOSPHATE BONDED |
SODIUM SILICATE BONDED |
|||||||||
|
Goods Brand |
NL70 |
NL60 |
NL45 |
GL85 |
GL70 |
GL60 |
GL50 |
GL42 |
DL80 |
DL60 |
LL75 |
LL60 |
LL45 |
LBN40 |
|
Al2O3(%) min |
70 |
60 |
45 |
85 |
70 |
60 |
50 |
42 |
80 |
60 |
75 |
60 |
45 |
40 |
|
CaO(%) max |
*** |
*** |
||||||||||||
|
Refractoriness(℃) min |
1760 |
1720 |
1700 |
1780 |
1720 |
1700 |
1660 |
1640 |
1780 |
1740 |
1780 |
1740 |
1700 |
*** |
|
Testing Temperature For Shrinkage after Reheating less than +/-1% (℃) min |
1450 |
1400 |
1350 |
1500 |
1450 |
1400 |
1400 |
1350 |
1500 |
1500 |
1500 |
1450 |
1350 |
1000 |
|
Cold crushing strength (MPa) after drying at 110℃min |
10 |
9 |
8 |
35 |
35 |
30 |
30 |
25 |
40 |
30 |
30 |
25 |
20 |
20 |
|
Bending strength (MPa) after drying at 110℃min |
2 |
1 |
5 |
5 |
4 |
4 |
6 |
5 |
5 |
4 |
*** |
|||
Send product request
Other supplier products
 |
Magnesium Alloy Ingot | Mark & model：Ingot weight: 7.5+0.5kg, 5+0.5kg, 15+0.5kg , etc. It can be made according to the buys' request. Origin：Asia and Pacific AreaChin... |
 |
Ferro Phosphorus | Mark & model：Size:10-60MM 90% MIN(As per buyer's option) FERRO PHOSPHORUS Brand Chemical Compositions % P Si C S Mn &le... |
 |
Fire clay brick SK | Quick Details Place of Origin:Shanxi, China (Mainland) Shape:Brick Material:Alumina Block Al2O3 Content (%):45-85% Refractoriness (Degree):1770&d... |
 |
Steel Fiber | Mark & model ： We can supply various kinds of steel fibers according to the buyers' requirements of materials, manufacturing processes, shapes ... |
 |
Silicon Nitride | FD90,95；FD99-α，FD99-β；FD3N；FD4N Siliconnitride Siliconnitridepowder,Gray,Anadvancedinorganicnon-metallicmaterials,Itiswidelyusedintheir... |