High Alumina Bricks for General Use
Mark & model：LZ-80、LZ-75、LZ-65、LZ-55、LZ-48
| HIGH ALUMINA BRICKS FOR GENERAL USE |
| Goods Brand |
LZ-80 |
LZ-75 |
LZ-65 |
LZ-55 |
LZ-48 |
| Al2O3(%) min |
80 |
75 |
65 |
55 |
48 |
| Refractriness under load 0.2 Mpa ( ℃) min |
1530 |
1520 |
1500 |
1450 |
1420 |
| Apparent porosity (%) max |
22 |
23 |
23 |
22 |
22 |
| Cold Crushing strength (MPa)min |
55 |
50 |
45 |
40 |
35 |
| Shrinkage after reheating (%) max |
1500℃x2h |
+0.1~-0.4 |
+0.1~-0.4 |
+0.1~-0.4 |
+0.1~-0.4 |
*** |
| 1450℃x2h |
*** |
*** |
*** |
*** |
+0.1~-0.4 |
| |
| Alumina-silicate products containing more than 48% of Al2O3 and in a certain shape, is called high alumina brick, widely used in blast furnace, thermal storage chamber, soaking pit, annealing furnace, ladle, etc. High alumina brick containing more than 80% or higher are used in electric arc furnace roof and the special zone of other high temperature furnaces. |
Other supplier products
|
|
Magnesium Powder, Magnesium Granule |
Below 100 meshes. It can be customized according to the specific demands of customers.
Origin：Asia and Pacific AreaChina |
|
|
Silica Brick |
Mark & model：GZ-96、GZ-95、GZ-94
SILICA BRICKS
Goods Brand
GZ-96
GZ-95
GZ-94
SiO2(%) min
96
95
94
Fe2O3(%) max
... |
|
|
Clay insulation brick |
Quick Details
Place of Origin:Shanxi, China (Mainland)
Shape:Brick
Material:Alumina Block
Refractoriness (Degree):Common (1580°< Refractor... |
|
|
Fire clay brick SK |
Quick Details
Place of Origin:Shanxi, China (Mainland)
Shape:Brick
Material:Alumina Block
Al2O3 Content (%):45-85%
Refractoriness (Degree):1770&d... |
|
|
Magnesium Alloy Ingot |
Mark & model：Ingot weight: 7.5+0.5kg, 5+0.5kg, 15+0.5kg , etc. It can be made according to the buys' request.
Origin：Asia and Pacific AreaChina... |
All supplier products
Same products