Glass furnace structure and various parts of refractory materials
Refractory materials are the main building blocks of glass melting furnaces and have a decisive influence on the quality of glass, energy consumption and even the cost of the product. The development of glass melting technology depends largely on the progress of refractories manufacturing technology and quality improvement. Glass Furnace Furnace Structure For large float lines, the glass kiln is usually constructed of L-shaped hanging wall (usually using silica bricks), melting section (fused glass in direct contact with glass, upper used (Usually using silica bricks), the cooling section including the ototoxic tank (where the corundum material is used in direct contact with the liquid glass, and silica brick or corundum is used where it is not in contact with the liquid glass), annealing Kiln, regenerator (made of clay, high aluminum, direct combination of magnesia-chrome brick) and other parts. Glass furnace main parts of the conditions of use and refractory choice
Glass melting furnace and cooling Department of the top (including the arch angle), the site is often at 1600 ℃ operating temperature, the use of refractory material in this area is subject to high temperature, load but also by the alkali steam and compound Therefore, the material used for the top must have high refractoriness, high load softening temperature and good creep resistance, and the thermal conductivity is small, the erosion of high temperature does not pollute the glass liquid, the bulk density is small, High temperature strength and other characteristics. The high-quality high-purity silica brick with just the above characteristics: 1, the load temperature close to the refractory; 2, high temperature stability, high strength; 3, due to the main component of SiO2, content> 96%, the same as the main components of glass , So erosion under high temperature basically does not pollute the glass liquid; 4, the price is cheap. Therefore, at present, in the top of large-scale glass, pure high-quality high-purity silica bricks become the glass of choice for manufacturers. The chemical attack caused by high temperature chemical reaction between fly ash, alkali vapor and refractory materials, as well as the change of the crystal form and the change of the structure due to temperature and phase migration are the main reasons for the damage of the top tile. The results show that the high-quality glass kiln silica brick is used in the top of 碹 roof, and the alteration process at high temperature is basically phase transformation and impurity migration. The chemical attack and melting effect are extremely slight. As a result of phase change and self-purification, the working belt gradually changes its performance and its high temperature performance is improved.
Другие товары поставщика
|
Ceramic Fiber Paper |
Typical Application:
♦ Welding thermal barriers♦ Castings parcel♦ Plant catalytic converters parcel♦ Ladle parcels♦ T... |
|
Fused Cast High Zirconia Block TY-Z88 TY-Z95 |
Fused cast high zirconia bricks descriptionThe series of TY-Z are fused cast high zirconia refractories which are specially designed refractory for... |
|
Плавлено-литых АЗС 36# блок |
Преимущества: ⦠компактная микроструктура ⦠Хорошая сопротивляемость эрозии в расплавленное стекло ⦠хороший тепловой шок сопротивления ⦠е... |
|
динасовый кирпич BG-96A BG-96B |
A brief introduction of silica brickSilica brick is a kind of acid refractory mainly made from tridymite, cristobalite and a small amount of resid... |
|
Silica Hot Repair and Mortar |
Directions for use of silica hot repairing mixThe silica hot repairing mix is used for hot repairing of silica brick crown top of glass furnace. Th... |
Все товары поставщика
Похожие товары