PA66 GF50(A2011J) for Engineering Plastics
PA66GF50is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added to be used in injection molding products.
Typical Application of PA66 GF50 (A2011J)
PA 6.6 GF50HB grade is applied to the field of industrial product structural parts, requiring high strength, high toughness, high and low-temperature resistance, and commonly used as water valve diverter and blade of air outlet, mechanical gears and bushings.
Other Details of PA6 6 GF50(A2011J)
Physical Property
|
Ash |
(50.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1538Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.1-0.3 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
Mechanical Properties
|
Tensile strength (217.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.5% I ISO527) Conditioned |
5mm/min |
|
Notched Impact Strength (17.0KJ/m2 I ISO179 Conditioned |
|
|
Flexural Strength (354 MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (14263 MPa I ISO178) Conditioned |
2mm/ min |
Thermal Property
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(260*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
290-310°C |
|
Nozzle Temperature |
290-310*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
As an experienced plastic engineering inc and masterbatch factory, Anmei Grouphas a professional team of senior engineers with 10-15 years of R&D experience in engineering plastics and masterbatch, we work together to achieve our goal of solution providing and create more values for customers with our stable quality and professional technical service, making a better life for human beings.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Nylon66 PA66 Halogen-free FR (A2005X01) for Engineering Plastics | Flame-retardant PA66FRis a halogen-free flame retardant engineering plastic made of nylon 66 resin as a base material (other fibers can also be add... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | PA66 GF 15Heat Stabilized (A2006C, A2016C) for Engineering Plastics PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resi... |
 |
Antibacterial Masterbatch | Polymer antibacterial masterbatchis a kind ofmasterbatch materialthat adds antibacterial agents into the carrier resin, which is offering antimicro... |
 |
PA66 GF20 With High Tensile Strength (A2307D, A2317D) for Engineering Plastics | Elastomer toughened nylon 66 with 20% glass fiber is called PA66 GF 20, it shows high oil resistance, high impact resistance, good resistance to lo... |
 |
Nylon 66 PA66 Heat Stabilized (A2006X01, A2016X01) for Engineering Plastics | Nylon66 PA66 Heat Stabilized Description Nylon66 PA66 Heat Stabilized a high temperature nylon made by the polycondensation of terephthalic acid a... |
Похожие товары
 |
Medical Plastic Parts | Продавец: Packson Mold Co.,Ltd | Project Management To be a qualified medical plastic components manufacturer, the most advanced ... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol... |
 |
PA66 GF | Продавец: Suzhou Anmei Material Technology Co., Ltd | Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif... |
 |
Nylon6 PA6 | Продавец: Suzhou Anmei Material Technology Co., Ltd | Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o... |
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a... |