PTFE Slide Bearing Plate
PTFE Slide Bearing Plates
The product is made of PTFE suspended fine powder resin, cold pressed into billet, sintering forming, pressing grease groove, machined into various specifications of sliding block. Has very high compressive strength, low friction coefficient, excellent aging resistance and chemical corrosion resistance, can be used for a long time to -180℃ to 260℃, good weather resistance. The products are widely used in high-speed rail, bridge and light rail projects, and have been recognized by customers in practical use.
The Technical Indexes of PTFE Slide Bearing Plate
|
Product name |
The implementation of standards |
The technical performance index |
Remarks |
||||
|
The proportion of |
(Mpa) Tensile strength |
Crack elongation |
Witstanding voltage |
||||
|
Molded sheet |
Oridinary type |
ZGB33002 SFB-1 & SFB-2 |
≥15 |
≥150 |
SFB-1≥10 |
||
|
Bridge use |
JT/T901-2014 |
≥30 |
≥300 |
||||
|
Skived sheet |
ZGB 33002 SFB-1 & SFB-2 |
≥15 |
≥150 |
SFB-1≥10 |
|||
Types and Specifications of PTFE Slide Bearing Plate
|
Name of commodity |
Diameter/Length of side(mm) |
Thickness(mm) |
|
Round plate |
140-1800 |
2-10 |
|
Square plate |
2000*2000 |
2-10 |
The Main Technical Indicators of PTFE Slide Bearing Plate
|
Items |
Density |
Tensile Strength |
Elongation at break |
Ball indentation hardness H132/60 |
|
Unit |
g/cm³ |
Mpa |
% |
Mpa |
|
JT/T901-2014 Standard |
≥30 |
≥300 |
Features of PTFE Slide Bearing Plate
Temperature resistance: It is able to work stably between -180°C to +260°C.
Excellent chemical corrosion resistance: Applicable medium includes oil, acid solution and almost all chemical materials.
Excellent non-sticky property: With low friction coefficient it easier to remove those resin, dopes, oil and other sticky things.
Anti-aging, weathering resistance.
Excellent insulation property.
Filled material: Filled PTFE productshas more outstanding performance by adding filler such as carbon, graphite, bronze, glass fiber, carbon fiber, MOS2, PEEK, PI, POB BaSO4, SiO2, glass bead, polyamide.
As a plastic industrial productsmanufacturer, we will do our best to meet all the needs of customers.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
PTFE Molded Tube | PTFE rods and tubes are sintered with PTFE suspension resin after moulding or hydraulic pressing, or extruded with PTFE presintered disperse resin ... |
 |
PTFE Machined Parts | PTFE machined partsare custom-made components manufactured from polytetrafluoroethylene material. These parts are created through machining process... |
 |
Glass Filled PTFE Products | Glass Filled PTFE Gaskets PTFE filled products by PTFE resin filler, after mixing, pressing and sintering after secondary processing. This product... |
 |
PTFE Extruded Tube | PTFE Extruded Tube Polytetrafluoroethylene extrusion tube process. mixing: through the mixing machine to polytetrafluoroethylene powder and ext... |
 |
PTFE Slide Bearing Plate | PTFE slide bearing platesare made of PTFE suspended fine powder resin, cold pressed into billet, sintering forming, pressing grease groove, machine... |
Похожие товары
 |
Medical Plastic Parts | Продавец: Packson Mold Co.,Ltd | Project Management To be a qualified medical plastic components manufacturer, the most advanced ... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol... |
 |
PA66 GF | Продавец: Suzhou Anmei Material Technology Co., Ltd | Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif... |
 |
Nylon6 PA6 | Продавец: Suzhou Anmei Material Technology Co., Ltd | Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o... |
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a... |