Degassing Flux (SATA-PF-350)
General Description of Degassing Flux (SATA-PF-350)
Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process.
SATA-degassing flux is a kind of traditional high efficiency degassing fluxfor aluminium and its alloys, it used for removing hydrogen and oxides from the aluminium melting.
Application of Degassing Flux (SATA-PF-350)
Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten.
Advantage of Degassing Flux (SATA-PF-350)
Easy operation, There are two options. One is with hexachloroethane in tablet form.and another is in powder form without hexachloroethane
It has excellent performance in refining, degassing and drossing
It can enhance the quality of casting, hydrogen content of aluminium molten can reduce to ≤0.1ml/100gAl, the oxide inclusion(Al2O3) can reduce 20% min, the casting inclusion defect reduce 50%min
Specification of Degassing Flux (SATA-PF-350)
White mixed powder
Aluminum degassing fluxis suit for all series alloy except high magnesium alloy,
Dosage: recommended dosage: 3%-5% large melting furnace, 4%-6% for crucible furnace
Working Temperature: 710℃-780℃
Package of Degassing Flux (SATA-PF-350)
Packed in 5kg (PE), 25kg (PP), 1000kg bags or customized.
Stored in dry, well-ventilated place, and avoid direct sunlight, keep sealed before using.
NOTE: This flux has serious hygroscopicity, please use immediately after opening.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Sodium-Free Refining Flux | General Description of Sodium-Free Refining Flux Aluminum alloys containing more than 2 % magnesium become brittle with sodium. This flux is a com... |
 |
Degassing Flux | Degassing Flux(SATA-PF-350) General Description of Degassing Flux (SATA-PF-350) Practice has proved that the hydrogen is the main cause of the pore... |
 |
Covering Flux-Csf1 | C sf1is fused flux which does not contain any form of sodium salt and does not cause the alloy to be brittle, suitable for all kinds of aluminum an... |
 |
Mg Alloy Flux | Magnesium alloyfluxhas a low melting point and small heat capacity. When heated in the air, it gets oxidized fast, and it is easy to burn when over... |
 |
Fluxes for Aluminum Alloy | General Description: Aluminum alloys containing more than 2 % magnesium become brittle with sodium. Feature: This flux is a compact covering and cl... |
Похожие товары
 |
Hot Melt Adhesive for Vacuum Insulation Panels | Продавец: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Vacuum Insulation Panels Supply & Technical Support Capabilities ... |
 |
Hot Melt Adhesive for Packaging | Продавец: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Packaging Bond Strength & Durability: Hot melt adhesives provide i... |
 |
Hot Melt Adhesive for Hygiene Products | Продавец: Foshan Rurga New Material Technology Co. ,Ltd | Hot Melt Adhesive for Hygiene Products refers to thermoplastic pressure‑sensitive adhesives ... |
 |
LSAW Steel Pipe & Tube | Продавец: HEBEI TIRICO PIPELINE CO.,LTD | LSAW Steel Pipe & Tube , or Longitudinal Submerged Arc-Welding Pipe (also known as SAWL ... |
 |
Anti-Corrosion Steel Pipe & Tube | Продавец: HEBEI TIRICO PIPELINE CO.,LTD | Anti-Corrosion Steel Pipe & Tube Anti-Corrosion Steel Pipe & Tube What Is an Anti... |