CERAMIC STRUCTURED PACKING
Ceramic structured packingis made up of many packing unit bodies that share the same geometry shape. Corrugated ceramic packing is called Kelapak packing abroad, it is also called high-efficiency packing, because its separation-efficiency is several times more than ten times of loose cops packing. Compared with loose cops plate Tower Packing. Corrugated plate ceramic packing has a great number of advantages such as high-efficiency, large thruput, low liquid holdup, unsharp amplification and good operability.
Normal iron content
Low iron content
Parameters of Ceramic Structured Packing
|
Type |
Specific Surface Aream2/m3 |
CorrugatedPlate thickness mm |
Heaping weightKg/m3 |
VoidVolume% |
PressureDrop mmHg/m |
TheoreticalPiecesm-1 |
LiquidLoad m3/m2h |
MaxFactorm/s (kg/m3)-1 |
|
100Y |
100 |
300 |
1 |
|||||
|
125Y |
125 |
330 |
85 |
1-1.5 |
||||
|
160Y |
160 |
370 |
84 |
2 |
||||
|
250Y |
250 |
420 |
80 |
2 |
||||
|
350Y |
350 |
470 |
78 |
|||||
|
400Y |
400 |
500 |
75 |
3 |
3 |
|||
|
450Y |
450 |
520 |
72 |
4 |
4 |
|||
|
550Y |
550 |
620 |
74 |
5-6 |
||||
|
700Y |
700 |
650 |
72 |
6 |
7 |
|||
|
100X |
100 |
280 |
92 |
1 |
||||
|
125X |
125 |
300 |
90 |
|||||
|
160X |
160 |
350 |
85 |
2 |
||||
|
250X |
250 |
380 |
80 |
|||||
|
350X |
350 |
450 |
78 |
3 |
||||
|
400X |
400 |
480 |
75 |
4 |
||||
|
450X |
450 |
500 |
72 |
3-4 |
||||
|
470X |
470 |
440 |
75 |
5 |
5 |
|||
|
550X |
550 |
620 |
74 |
5-6 |
||||
|
700X |
700 |
650 |
72 |
6 |
7 |
|
SiO2 |
Al2O3 |
Fe2O3 |
CaO |
MgO |
Other |
|
≥72% |
≥23% |
≤0.5% |
≤1.0% |
≤0.1% |
|
Specific weight |
Water adsorption |
Acid resistance |
Crushing strength |
Operation temperature |
Moh’s hardness |
Ignition lost |
|
≤0.5% |
>99.5% |
≤1000℃ |
≥130Mpa |
≥7 |
≤5.0% |
Advantage of Ceramic Structured Packing
The most economical range of this structured tower packing is F-factor 1.5-2.0
The pressure drop of each theoretical sheet is 0.3-1 mbar
The minimum liquid load of the ceramic tower packing is 2001/m2h
A distributor should be installed for every 3-4 meters inside packing towers with diameters of more than 300 mm
Application of Low Iron Content Ceramic Packing
Fining process of corrosive mixtures, which have strict requirements for pressure drop and number of theoretical sheets.
Vacuum treatment under absolute pressure higher than 1 mbar.
Fining and Distillation of halogen organic compounds.
Why People Choose
NAIKE CHEMICAL
NAIKE is a longstanding partner, don't hesitate to contact us!
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
CARBON MOLECULAR SIEVE | ChinaCarbon Molecular Sieve PSA (pressure swing adsorption) nitrogen generation is implemented by the selective adsorb characteristic of CMS, an... |
 |
CERAMIC BALL | Ceramic Balls for Sale The alumina ceramic ballsproduced by our company are mainly divided into the following categories: Inert alumina balls... |
 |
13X Molecular Sieve | 13X Molecular Sieve is the sodium form of the type X crystal and has a much larger pore opening than the type A crystals. 13X Molecular Sieve will ... |
 |
MCM-41 Zeolite | MCM-41 show potential on catalytic cracking, residue hydrocracking, lube oil hydro finishing, alkylation, olefin polymerisation, separation of CO2 ... |
 |
CERAMIC BALL | The ceramic balls produced by our company are mainly divided into the following categories: Inert alumina balls Activated alumina ceramic balls Gr... |