Смола-специфической адсорбции золота

Indicator Parameter
Functional group -N+(CH3) 2H2O
Appearance Milky white opaque sphere
Finished form CLˉ
Moisture content % 45-55
Weight whole exchange capacity mmol/g ≥5.0
Volume whole exchange capacity mmol/ml ≥1.50
Wet density g/ml 1.05-1.1
Wet real density g/ml 0.68-0.75
Particle size range % (0.6-1.80mm)≥95%
Granularity (<0.6mm)≤1.0
Uniformity coefficient 1.5
Sphere rate after abrasion % ≥95%
Indicator Parameter
Regeneration concentration HCl:2-4%;/NaOH:2-4%
pH range 1-10
Highest use temperature℃ OH-100/Cl-40
Expansion rate (OHˉ→Clˉ)% ≤15-20%
Operational flow speed m/h 10-30
Desorption : "Resin adsorption of gold thiourea with 9% + 3% sulfuric acid analysis, analytical dosage of 6-8 times the bed volume, contact time with Resin for 2h or more.
"
Regeneration process: Resin after resolution after washing, rinse with 2-3 times the bed volumeNaOH, about 1 hour, then rinse renewable HCl solution, the dosage is 2 times the bed volume, time is about 1.5h, washed clean and odor can be the last. (Regeneration concentration reference Reference of indicator)
Другие товары поставщика
|
|
Сульфид натрия |
Class 1 Class 2 Class 3
Test items Superior grade A first-rate product Acceptable product A first-rate product Acceptable product
Sodium Sulphi... |
|
|
Калия цианид |
Test items Index
Shape Lump
Potassium cyanide (KCN) % ≥99.0
Potassium hydroxide(KOH) % ≤0.3
Potassium carbonate(K2CO3)% ≤0.4
Potassi... |
|
|
Соляная кислота |
Item Index
Total acidity(HCI) ≥ 31.0
Iron(Fe) ≤ 0.002
Residue on ignition % ≤ 0.05
Free chlorine(CI)% ≤ 0.004
Arsenic(As)% ≤ 0.... |
|
|
Триоксид мышьяка |
Main content Other impurities
Arsenic trioxide Iron Lead Chlorine Chromium Cadmium Water
As2O3 Fe Pb Cl Cr Cd H2O
≥ ≤ ≤ ≤ ≤ &l... |
|
|
Полиэ фирполиол |
Model Hydroxyl value Water content Acid value pH value Potassium Chromaticity Viscosity Degree of unsaturation
mgKOH/g % mgKOH/g mg/Kg APHA mPa.s/... |
Все товары поставщика
Похожие товары