Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02
During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all defects.
The cause of the cracks in the bearing rings is complicated. From the raw materials to the finished products of the ferrules, if the process is not proper, the cracks may be directly caused or the hidden cracks may be buried for the occurrence of the lap ring grinding cracks.
There are many ways to form cracks in bearing rings: Raw material defects include: cracks in raw materials and the effects of raw material defects on the grinding process.
Forging defects include forging cracks, effects of forged microstructure defects on the grinding process, and cutter cracks. There are also various heat treatment defects and the like. Therefore, crack detection and hardness testing are essential. As one of the experienced non destructive testing equipmentmanufacturers, BKNoffers the perfect combination of Bearing Ring Crack and Hardness Combination testing equipment. Our advanced crack testing equipmentenable accurate and efficient crack detection, ensuring the quality and integrity of forged components.
Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02 Brief Introduction
Detection process
Vibrating plate and string charging →hardness test→crack detection→automatic blanking
↓
Bad product sorting
Automatic charging —automatic detection—automatic sorting —automatic blanking
Crack sensitivity: a crack with a depth of ≥0.05 mm and a length of ≥1 mm extending inward from the surface of the ferrule; for a crack that has not extended to the surface inside the ferrule, when the thickness between the subcutaneous surface and the surface of the workpiece is ≤0.2 mm, the depth is ≥0.20 mm Cracks of length ≥ 1 mm can be detected.
Hardness sensitivity: Rockwell 1HRC ~ 2HRC (other parameters remain stable and consistent).
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
EDM Notch | An electric pulse is a pulse generated by electrons, and a pulse is a process of changing a voltage in a short time. Electropulsing is an unsteady ... |
 |
BKNET-101 Automatic Eddy Current Testing | The technology of BKNoriginated from eddy current Laboratory of Institute of Materials, Nanjing University of Technology. At present, it is a leadi... |
 |
Valve Tappet Eddy Current Flaw Detector QMTZET-04 | Tappet full automatic eddy current testing system is a full automatic crack hardness sorter that integrates light, electricity and machinery. The w... |
 |
Connecting rod hardness eddy current sorting machine LGYDFX-01 | The connecting rod hardness eddy current sorting machinehas a calibration device, input compensation parameters, automatic/manual temperature compe... |
 |
ECT For Automotive And Aerosapce | NDT Application in Automotive Industry: Eddy current testing NDT echnology has been widely used in the detection of metal components in the autom... |
Похожие товары
 |
Электронная окулярная камера MECHANIC MEC 4K 2K HD для стереомикроскопа | Продавец: ШЭНЬЧЖЭНЬСКАЯ ТЕХНОЛОГИЯ PHONEFIX, LTD (КИТАЙСКИЙ PHONEFIX) | Описание Электронная окулярная камера Mechanic MEC 2K/2K PRO/4K HD может превратить бинокулярный ... |
 |
Цифровой мультиметр Fluke 15B+ 17B+ 18B+, тестер напряжения и частоты | Продавец: Шэньчжэнь Weike Repair Technology Co., Ltd. | Полупрозрачная/полностью прозрачная/молочно-белая/светло-желтая паяльная паста iFixes 10CC， не со... |
 |
HTT-02 Hot Tack Tester | Продавец: Cell Instruments Co., Ltd | The HTT-02 Hot Tack Testeris specifically designed to assess this property by measuring the stren... |
 |
SPC-01 Stretch Film Peeling Cling Tester | Продавец: Cell Instruments Co., Ltd | The SPC-01 Stretch Film Peeling Cling Testermeasures the adhesion between two layers of stretch f... |
 |
FTT-01 Film Thickness Tester | Продавец: Cell Instruments Co., Ltd | The FTT-01 FilmThickness Testerutilizes a mechanical scanning technique to measure the thickness ... |