S5 Cold Work Tool Steel Plates Bars Sheet Forgings
Preheating: Heat at a rate not exceeding 400°F per hour (222°C per hour). For complex and large tools, heat to 1150-1250°F (621-677°C) and equalize. Then heat to 1300-1400°F (704-760°C) and equalize. For simple geometries, use only the second preheating temperature range.
S5 Shock-Resisting Tool Steel is a silicon-manganese tool steel which exhibits the highest impact toughness among all of the "S" type steels. The high toughness and the ability to be hardened to 62 Rockwell C make S5 an excellent choice for applications that require higher strength than S7 shock-resisting tool steel. The steel is typically hardened using an oil quench, but for simple geometries, the steel may be water quenched.
APPLICATIONS: Pneumatic tools, shear blades, mandrels, heavy-duty punches, and stamping dies.
COMPOSITION
C |
Mn |
Si |
Cr |
Mo |
V |
PHYSICAL PROPERTIES
Density: 0.280 lb/in3(7750 kg/m3)
Specific Gravity: 7.75
Modulus of Elasticity: 30 x 106 psi (207GPa)
Machinability: 65-70% of a 1% carbon steel
HARDENING
Critical Temperature:Ac1: 1410°F (766°C)
Preheating: Heat at a rate not exceeding 400°F per hour (222°C per hour). For complex and large tools, heat to 1150-1250°F (621-677°C) and equalize. Then heat to 1300-1400°F (704-760°C) and equalize. For simple geometries, use only the second preheating temperature range.
Austenitizing (High Heat): Heat slowly from the preheat. For Oil Quenching: 1600 - 1700°F (871 - 927°C) For Water Quenching: 1550 - 1650°F (842 - 899°C) Soak for 30 minutes for the first inch (25.4 mm) of thickness, plus 15 minutes for each additional inch (25.4 mm) of thickness.
Quenching: Oil or water to 150-125°F (66-51°C).
Tempering: Temper immediately after quenching. Hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum, then air cool to ambient temperature. To minimize internal stresses in cross sections greater than 6 inches (152.4 mm) and to improve stability in tools that will be EDM’d after heat treatment, a soaking time of 4 to 6 hours at the tempering temperature is strongly recommended.
Cryogenic Treatment: Some prefer to do cryogenic treatment as an extension of the quench from the austenitizing treatment. Others prefer to cryogenically treat after tempering.
:Hubei Risunsteel Co., Ltd.
ANNEALING
Annealing must be performed after hot working and before re-hardening.
Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1425 - 1475°F (773 - 801°C), and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 229 HBW.More information .
,based on the over one hundred years’s production history of in Huangshi, provide professional services and material for cutting tool companies, mould companies and other industrial enterprises all over the world for years.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
S5 Cold Work Tool Steel Plates Bars Sheet Forgings | Preheating: Heat at a rate not exceeding 400°F per hour (222°C per hour). For complex and large tools, heat to 1150-1250°F (621-677&de... | |
High toughness H13 1.2344 SKD61 Hot Work Tool Steel | Product Details Chemical Composition (%) Standard Steel Grade C Si Mn P S Cr Mo V W DIN - ASTM H13 ... | |
1.2316/3Cr17Mo Plastic Mold Tool Steel Plates Bars Sheet Forgings | Product Details Specification Round bar Diameter(mm) Length(mm) - Forged round bar:φ50~450 2000~6000 - Rolled round bar:&... | |
45CrNi4Mo/1.2767 Hot Work Tool Steel Plates Bars Sheet Forgings | Product Details Chemical composition C Mn Si Cr V Mo P S - ≤0.03 ≤0.03 Equivalent grades: DIN AFNO... | |
Cr12Mov Cold Work Tool Steel Plates Bars Sheet Forgings | Used to manufacturing all kinds of moulds and tools with comparatively larger cross sections and complex shapes, which can bear heavy shock loads.... |
Похожие товары
Радиальные шарикоподшипники серии 6000 | Продавец: Ningbo Yuhong Bearing Co., Ltd | Радиальные шарикоподшипники серии 6000 представлены в различных размерах и конфигурациях. Эти под... | |
Прямая труба из хромоникелевого сплава центробежного литья | Продавец: Нанкин Xinshuo Механическое оборудование Лтд | Прямая труба из хромоникелевого сплава центробежного литьяДля получения дополнительной техническо... | |
White Iron Wear Blocks, Wear Bars | Продавец: Yiwu WALKSON Machinery Equipment Co., Ltd. | The unique, formable designed wear bars is available in various lengths, grades and sizes and can... | |
TITANIUM ALLOY STEEL TUBE | Продавец: YUHONG GROUP CO., LIMITED ZHEJIANG YUHONGWELL STEEL CO., LIMITED | TITANIUM ALLOY STEEL TUBE Titanium is the ninth most abundant element in the earth's crust and t... | |
STEEL FITTING | Продавец: YUHONG GROUP CO., LIMITED ZHEJIANG YUHONGWELL STEEL CO., LIMITED | STEEL FITTING Steel has been used for making pipe and pipe fittings for years for its durability... |