PE heat shrink film/package film
Heat shrink film
Technical parameters:
Width: single 0.2m~9m
Tear strength: horizontal ≥40kn/m
Vertical ≥40kn/m
Thickness: 0.015mm~0.35mm
Tensile strength: horizontal：≥17mpa Vertical≥17mpa
Shrinking percentage: horizontal 15%~30% Vertical 50%~70%
Elongation at break：≥350%
Shrinkage temperature: 120℃~180℃
Core inner diameter：76mm
Proportion: 0.925g/cm3
Advantage:
1.Strong puncture resistance
2. Unusual self-adhesive property.
3. High grade of transparency and glossiness
4.Strong tear resistance, with good printing adaptability.
5. Strong shrink memory function, good retraction tightness.
6. Good flexibility and stretch ability, strong wrapping ability.
7. Large longitudinal shrinkage ratio, large range of shrinkage, strong assembly packaging ability.
Application: medicine, drink, spring water, beer, composite floor, building materials , waterproof rolling material, metal products, dairy products, glass bottle, industrial paper and so on.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Self adhesive Bitumen Waterproof Membrane manufacturer | Self-adhesive Bitumen Waterproof Membrane (without reinforcement) Self-adhesive Bitumen Waterproof Membrane (with reinforcement) Introduction: The... |
 |
Embossed PP release film for self adhesive bitumen waterproof membrane | Embossed PP release film Release material for waterproof membrane easy to construct,environmental,recyclable Thickness:0.027--0.040mm |
 |
reinforced metal aluminum foil used as surface material | Reinforcing metal aluminum foil Reinforcing metal aluminum foil is the metal aluminum foil covered with PET film. The metal aluminum foil is easy t... |
 |
0.1mm PET film used as surface material of waterproofing membrane | Reinforcement film Characteristic: Application: waterproof rolling material reinforcement film Color: red, blue, white and plastic primary color, c... |
 |
POF heat shrink film/package film | Its main advantage is excellent hot slip property.When the film without hot slip property,the hot surface after shrink causes stick,which makes you... |