PE heat shrink film/package film
Heat shrink film
Technical parameters:
Width: single 0.2m~9m
Tear strength: horizontal ≥40kn/m
Vertical ≥40kn/m
Thickness: 0.015mm~0.35mm
Tensile strength: horizontal：≥17mpa Vertical≥17mpa
Shrinking percentage: horizontal 15%~30% Vertical 50%~70%
Elongation at break：≥350%
Shrinkage temperature: 120℃~180℃
Core inner diameter：76mm
Proportion: 0.925g/cm3
Advantage:
1.Strong puncture resistance
2. Unusual self-adhesive property.
3. High grade of transparency and glossiness
4.Strong tear resistance, with good printing adaptability.
5. Strong shrink memory function, good retraction tightness.
6. Good flexibility and stretch ability, strong wrapping ability.
7. Large longitudinal shrinkage ratio, large range of shrinkage, strong assembly packaging ability.
Application: medicine, drink, spring water, beer, composite floor, building materials , waterproof rolling material, metal products, dairy products, glass bottle, industrial paper and so on.
在线联系供应商
Other supplier products
 |
Self adhesive Bitumen Waterproof Membrane manufacturer | Self-adhesive Bitumen Waterproof Membrane (without reinforcement) Self-adhesive Bitumen Waterproof Membrane (with reinforcement) Introduction: The... |
 |
China PE release film/ release liner manufacturers, suppliers | PE release film Products overviews: PE release film refers to the film with separative film on the surface. PE release film does not have viscidit... |
 |
POF heat shrink film/package film | POF heat shrink film/package film Its main advantage is excellent hot slip property.When the film without hot slip property,the hot surface after s... |
 |
100 Micron PET film used as bitumen waterproof membrane reinforcement | Reinforcement film Characteristic: Application: waterproof rolling material reinforcement film Color: red, blue, white and plastic primary color, c... |
 |
POF heat shrink film/package film | Its main advantage is excellent hot slip property.When the film without hot slip property,the hot surface after shrink causes stick,which makes you... |