ZG-P-8086/ZG-I-9823
Super high-hardness and super low-density PU Resin for shoe sole
Characteristic: Super-high hardness, super-low density.
Application: Applicable to the production of shoe soles for both men and women
Typical properties of PU Resin
|
Name of products |
Appearance |
Viscosity（Pa·s/50℃） |
Density（g/cm3/40℃） |
Package（kg） |
|
ZG-P-8086 |
White or pale yellow, liquid, no foreign material |
18 |
||
|
ZG-I-9823 |
Transparent liquid, no foreign material |
20 |
Reference shipments ratio: A/B=28/25(barrel)
Catalysts and auxiliary agents
ZG-P-8086/ZG-AC-2/water =18kg/230g/70-120g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties:
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratioP+C/I |
100/98-102 |
Molded density of sole（g/cm3） |
|
|
Using temperature（℃） |
material: 45-50; B material: 38-42 |
Hardness (type A) |
75~80 |
|
Cream time（s） |
6~9 |
Tensile strength（MPa） |
— |
|
Rise time（s） |
30~45 |
Elongation（％） |
— |
|
Metal mold temperature（℃） |
55~65 |
NBS abrasion resistance（％） |
≥10% |
|
Demould time（min） |
Free foam density（g/cm3） |
||
|
Folding endurance (room temperature)(40,000 gap length mm) |
— |
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
More information can view .
Send product request
Other supplier products
 |
ZG-P-6955 / ZG-I-8308 | Low-hardness and medium-density shoe sole PU Resin for casual shoes for both men and women Characteristic: Low hardness, medium density. Ap... |
 |
ZG-P-6570/ZG-I-5012 | ZG-P-6570/ZG-I-5012,, Dual density PU Resin for labor protection shoes (safety shoe) sole Characteristic: Medium and low hardness, medium and hig... |
 |
China Medium Hardness Sole PU Resin | ZG-P-5005/ZG-I-5320 Medium and high-density PU Resin for shoe sole with the upper Characteristic: Medium and low hardness, medium and high densit... |
 |
ZG-P-6955 / ZG-I-8308 | ZG-P-6955 / ZG-I-8308,PU Resin For Casual Shoes,High Density Low Hardness Sole Pu PU Resin For Casual Shoes High Density Low Hardness Sole Pu Low-h... |
 |
ZG-P-6687/ZG-I-5002 | Q/ZHTY 01—2010 Characteristic: High hardness, medium and high density good resilience Application: Applicable to the production of low-spe... |