ZG-P-6955 / ZG-I-8308
Low-hardness and medium-density shoe sole PU Resin for casual shoes for both men and women
Characteristic: Low hardness, medium density.
Application: Applicable to the production of casual shoes for both men and women.
Typical properties of PU Resin
|
Name of products |
Appearance |
Viscosity（Pa·s/50℃） |
Density（g/cm3/40℃） |
Package（kg） |
|
ZG-P-6955 |
White or pale yellow, liquid, no foreign material |
18 |
||
|
ZG-I-8308 |
Transparent liquid, no foreign material |
20 |
Reference shipments ratio: A/B=31/23(barrel)
Catalysts and auxiliary agents:
ZG-P-6955/ZG-AC-2/water=18kg/300g/60-80g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties:
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratioP+C/I |
100/62-66 |
Molded density of sole （g/cm3） |
|
|
Using temperature（℃） |
material: 45-50; B material: 38-42 |
Hardness (type A) |
40~55 |
|
Cream time（s） |
7~9 |
Tensile strength（MPa） |
|
|
Rise time（s） |
30~45 |
Elongation（％） |
350~450 |
|
Metal mold temperature（℃） |
45~55 |
NBS abrasion resistance（％） |
≥10% |
|
Demould time（min） |
Free foam density（g/cm3） |
||
|
Folding endurance (room temperature)(40,000 gap length mm) |
＜8 |
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
More information can view .
Send product request
Other supplier products
 |
ZG-P-6570H/ZG-I-7118 | ZG-P-6570H/ZG-I-7118 PU Resin for shoe sole with the upper Characteristic: Medium and low hardness, medium and high density Application: Applicab... |
 |
ZG-P-5080/ZG-I-5002 | ZG-P-5080/ZG-I-5002,High Density High Hardness Sole Pu,Low-Hardness Shoe Sole PU Resin High Density High Hardness Sole Pu Low-Hardness Shoe Sole PU... |
|
|
ZG-P-7165/ZG-I-724 | ZG-P-7165/ZG-I-7249,Poly ISO For Shoe Sole,High Density Low Hardness Sole Pu Poly ISO For Shoe Sole High Density Low Hardness Sole Pu Medium and lo... |
 |
ZG-P-6687/ZG-I-5002 | Q/ZHTY 01—2010 Characteristic: High hardness, medium and high density good resilience Application: Applicable to the production of low-spe... |
 |
ZG-P-8130/ZG-I-8260 | ZG-P-8130/ZG-I-8260 PU Resin for shoe sole of cold-resistant shoes Characteristic: Medium hardness, medium and low density, cold resistance and s... |