PA6 GF15 With High Tensile Strength (A1307C, A1317C) for Engineering Plastics
PA6 GF15with high tensile strength is made by 15% glass fiber reinforced, toughened, polyamide 6 resin for injection molding.
Typical Application of PA6 GF15with high tensile strength (A1307C)
PA6 with 15% glass fiber toughened plastics, due to its excellent properties, good appearance and easy processing characteristics, which has been successfully applied to the electrical field such as switches, controllers, the auto field such as heat dissipation barriers, accumulator shells, coolant pots, and the mechanical filed such as electric drill and motor housing, pump impeller, pulley, tool handle and bearing.
Processing Detail of PA6 GF15 with high tensile strength (A1307C)
Other Details of PA6 GF15 with high tensile strength (A1307C)
Physical Property
|
Ash |
(15.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1180Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.5-0.7 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.7-1.1% I ISO294-4) |
Mechanical Properties
|
Tensile strength(115.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break(2.0% I ISO527) Conditioned |
|
|
Notched Impact Strength(125 0MPa I ISO527) Conditioned |
2mm/min |
|
Flexural Strength(175MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus(5250 MPa I ISO178) Conditioned |
5mm/ min |
Thermal Property
|
Melting Point |
(220°C I ISO11357) |
|
Hot Deformation Temperature |
(175*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
240-260°C |
|
Nozzle Temperature |
240-260*C |
|
Tooling Temperature |
80*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
Want to buy masterbatch, contact us.
在线联系供应商
Other supplier products
 |
Anmei-PA6 GF for Engineering Plastics | As an engineering plastic company, Anmei focuses on the production of modified engineering plastics, among which high-performance nylon 6 engineeri... |
|
|
PA6 GF15 With High Tensile Strength (A1307C, A1317C) for Engineering Plastics | PA6 GF15with high tensile strength is made by 15% glass fiber reinforced, toughened, polyamide 6 resin for injection molding. Typical Applicatio... |
 |
PA66 GF50(A2011J) | PA 66 GF 50is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various process... |
 |
PA66 GF30 Halogenated FR (A2014F, A2114F) for Engineering Plastics | PA66 GF30FR is a Nylon 66 with 30% glass-fibers and flame retardant halogenated. Typical Application of PA66 GF30 Halogenated FR (A2014F) The adv... |
 |
Antibacterial Masterbatch | Polymer antibacterial masterbatchis a kind ofmasterbatch materialthat adds antibacterial agents into the carrier resin, which is offering antimicro... |
Same products
 |
COLMAST®CW1350（白色母粒） | 卖方: ADC PLASTIC., JSC | COLMAST CW1350因其突出的优点和与不同类型的初级塑料树脂（PP、PE、ABS...）的结合而成为完美的选择，白色母粒越来越广泛地应用于编织袋、塑料制品的注塑等。 .. 请访问我们的... |
 |
CALMAST®MN570 – PP碳酸钙填充母粒 | 卖方: ADC PLASTIC., JSC | CALMAST MN570 是帮助塑料制品制造商优化成本并提高机械和物理性能（例如耐热性、表面改善、提高成品的撕裂强度和拉伸强度）的完美选择。 特别是提高最终产品加工的稳定性。 请访问我们的网... |
 |
CALMAST®MF530 – PP碳酸钙填充母粒 | 卖方: ADC PLASTIC., JSC | CALMAST MF530 是帮助塑料产品制造商优化成本并提高机械和物理性能（例如耐热性、表面改善、提高成品的冲击强度和拉伸强度）的完美选择。 特别是提高最终产品加工的稳定性。 请访问我们的网... |
 |
PA6 GF30 Halogen-free FR (A1015F) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | PA6 FRis a PA6 with 30% glass-fibers and flame retardant free of halogens. Typical Applicati... |
 |
PA6 GF30 Halogenated FR (A1014F) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | PA6 GF 30 FRis a PA6 with 30% glass-fibers and halogens flame retardant. PA6 GF30 Halogenated ... |