CA Series-550CA30 PEEK Carbon Fiber Reinforcement
CA Series-550CA30peek carbon fiberreinforcement is a 30% carbon fiber reinforced naturalPEEK material, the addition of carbon fiber significantly increased the material's wear resistance and high temperature mechanical strength, thermal conductivity is pure resin G series 3 times.
Specification of CA Series-550CA30 PEEK withCarbon FiberReinforcement
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
|||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
℃ |
343 |
|
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
|
Amorphous |
gcm-3 |
|||
|
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
|
by immersion |
Equilib riu m,23℃ |
% |
||
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
|
23℃,50kHz |
3 |
|||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
Ω cm |
10 9 |
||
More kinds of peek composite material, please visit our website.
Send product request
Other supplier products
 |
ZYPEEK PEEK Raw Materials | PEEK polymer raw material is a kind of semicrystalline aromatic polvmer and its main chain of macromole is consist of arvl. ketone, and ether. PEEK... |
 |
Compression Molding Peek | Compression Molding PEEK PEEK has excellent corrosion resistance, radiation resistance, high-temperature resistance, low-temperature resistance,... |
 |
Grade GL Glass Filled Fiber Reinforced PEEK | PEEK-GL series, is a glass fiber composite modified PEEK glassmaterials, currently available from 5% -35% of different mass fractions of reinforced... |
 |
Grade CA Carbon Fiber Reinforcement PEEK | PEEK-CA series reinforced plastics filled with carbon fiber, high elastic modulus, mechanical strength, creep resistance, wear resistance and dynam... |
 |
CA Series-770CA30 PEEK Carbon Fiber Reinforcement | CA Series-770CA30 carbon fiber filled PEEKreinforcement is widely used in automobile and aviation fields. It is widely used in automobile fuel pump... |
Same products
 |
NOZZLE WEAD900121018D NOZZLE VDL95S6250 | Seller: China lutong | NOZZLE WEAD900121018D NOZZLE VDL95S6250Chris NOZZLE ZCK160P3125TNOZZLE ZCK150S3165NOZZLE ZCK150S... |
 |
Potable Water Storage Tank | Seller: 854818 | Potable Water Storage Tank In strict accordance with the content of the international water safet... |
 |
Nozzle Sprayer DLLZ157P964 Nozzle Sprayer DLLA148P2382+ | Seller: China lutong | Nozzle Sprayer DLLZ157P964 Nozzle Sprayer DLLA148P2382+Chris Whats/ app:+8–6–1&ndash... |
 |
luminous pigmen ment | Seller: 成飞经理，15813639200：李老师 后面华兴玻璃厂 ，高速大丰田阿波罗 集美天成 | ``Dan qin cha ban sheng`` if hears`s so you love. |
 |
titanium sputtering targets | Seller: Advanced Targets Materials Co., Ltd | titanium sputtering targets Titanium used in a wide variety of products such as watches, dr... |