Instructions of Epoxy Zinc-Rich Primer
It is two components epoxy zinc-rich primer heavy corrosion by a zinc primer, epoxy resin and other components. On steel surface treated to form a hard, wear-resistant, durable film, and provide long-lasting cathode protection.
Property of Zinc Rich Epoxy Primer Paint
Application of The Zinc Rich Epoxy Primer
Widely applicable to long-term anti-rust primer for steel primer, primer and maintenance, ships, bridges and other steel structures. Especially suitable for industrial, chemical, steel and other heavy-duty offshore matching primer coating.
Surface Preparation of The Epoxy Zinc-Rich Prime
The surface roughness of steel welds, rounded edges and clear the splash-melt welding, cleared the surface of the grease, oil and other pollutants; surface sandblasted to ISO standard Sa2.5 level or power tools rust St3 level; surface roughness of 50-85um, before spraying to ensure the surface is dry and clean.
The weather is good, the substrate temperature of not less than 5 ℃, relative humidity <85%. It must have good ventilation conditions in confined areas to ensure proper drying of the film. Before fully cured coating should not be exposed to oil, chemicals or mechanical stress.
Coating Application of Zinc Rich Epoxy Paint
Mixing mass ratio: Base material (A): The curing agent (B) = 10: 1.
Theoretical amount: 220 g / m2.
Painting passes: spraying or brushing 2 to 3, 60 to 80 microns dry.
Mixing: Use a power mixer component A (base) Stir, then stirring state by mixing ratio of the added amount of group B (curing agent), and fully mixed, while stirring continued momentum needed painting.
Thinner or Cleaner: For supporting diluent.
Curing time: After mixed directly.
After mixing pot life: 5 hours (23 ℃).
The Construction Method of Epoxy Zinc-Rich Prime
Brush: Recommended for small areas, acute sites and pre-coated and refinishing, but must meet the specified dry film thickness.
Spraying: airless spray or air spray, the airless spray is recommended priority.
Air spray: a discharge pressure 0.4-0.7Mpa, nozzle diameter 1.8-2.2mm;
Airless Spray: discharge pressure 15Mpa, nozzle diameter 0.43-0.48mm;
* When used in spray paint, because the need to adjust the viscosity, can be added to a thinner 0-10%.
Precautions
Shelf Life of The Epoxy Zinc-Rich Prime
Twelve months from the date of manufacture in the original unopened container at 32°C. Subject to re-inspection thereafter. Store in dry, shaded conditions away from sources of heat or ignition.
Package: 20 kg/ barrel.
Contact us get more details about Epoxy Zinc-Rich Primer Coating, such as TDS, Application Method, OEM etc.
Send product request
Other supplier products
 |
elf-cleaning & Anti-tracking Coating SRTV | Well solve the hydrophobicity loss problem of silicone rubber external insulation when in continual rainy and wet weather. It also helps to lessen ... |
 |
Multifunctional Insulator Cleaning Agent RS-10 | Multifunctional Insulator Cleaning Agent (RS-10) is mainly used for eradicating dirt, dust and contaminations on surface of the power equipment, es... |
 |
Anti-Algae & Anti-Fouling Coating | Leveraging upon our experience, we have become a prominent Anti-Algae & Anti-Fouling Coatings (RTV-ZB) Manufacturer, Exporter and Supplier in C... |
 |
Line Post Insulator | We can offer different Voltage of Line Post Insulator for Transmission Line. Such as Long Rod Insulator, Rod Insulator and Pin Type Insulator. Con... |
 |
Composite Insulator | We offer different kinds of composite insulator for substation. Contact us get more details about composite insulator, such as TDS, Application Met... |